Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 60.0 - 80.0 MPa | 8700 - 11600 psi | Injection; ISO 527 |
Raschig Group 6552 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Tensile Strength, Yield | 60.0 - 80.0 MPa | 8700 - 11600 psi | Injection and Compression; ISO 527 |
Raschig Group EPOXIDUR® 3582 EP Epoxy Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Moldi.. |
|||
Tensile Strength, Yield | 50.0 - 80.0 MPa | 7250 - 11600 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 183 MF Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18.. |
|||
Tensile Strength, Yield | 58.0 - 80.0 MPa | 8410 - 11600 psi | Average value: 69.0 MPa Grade Count:3 |
Overview of materials for Polyphthalamide (PPA), High Impact This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, High Impact". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Yield | 60.0 - 80.0 MPa | 8700 - 11600 psi | Average value: 68.9 MPa Grade Count:4 |
Overview of materials for Acetal Homopolymer, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Glass Fiber Reinforced". Each property range of values reported is minimum and maxim.. |
|||
Tensile Strength, Yield | 49.6 - 80.0 MPa | 7200 - 11600 psi | Average value: 61.7 MPa Grade Count:213 |
Overview of materials for Polycarbonate, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Unreinforced, Flame Retardant". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Yield | 28.0 - 80.0 MPa | 4060 - 11600 psi | Average value: 60.1 MPa Grade Count:26 |
Overview of materials for Nylon 6, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Film Grade". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Tensile Strength, Yield | 50.0 - 80.0 MPa | 7250 - 11600 psi | Average value: 62.7 MPa Grade Count:9 |
Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether + Styrene-Butadiene Blend". Each property range of values reported is minimum and ma.. |
|||
Tensile Strength, Yield | 30.0 - 80.0 MPa | 4350 - 11600 psi | Average value: 58.1 MPa Grade Count:8 |
Overview of materials for Epoxy, Molded, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Glass Fiber Filler". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Yield | 22.0 - 80.0 MPa @Temperature -40.0 - 80.0 °C |
3190 - 11600 psi @Temperature -40.0 - 176 °F |
Average value: 51.0 MPa Grade Count:2 |
Overview of materials for Acetal Copolymer, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Impact Modified". Each property range of values reported is minimum and maximum values.. |