Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 135 MPa | 19600 psi | ISO 527, ASTM D638 |
Nilit Nilamon B3 H7 GK 35 15% Glass Fiber, 25% Mineral Reinforced PA6 Description: Nilamon B3 H7 GK 35 provides a combination between low warpage and high stiffness, while retaining a good impact strength. It has a high heat aging resistance, so that it is suitable fo.. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ISO 527-2 |
PolyOne Nymax™ ND 1233 GF Black Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
Tensile Strength, Yield | 135 - 135 MPa @Temperature 130 - 175 °C |
19600 - 19600 psi @Temperature 266 - 347 °F |
Average value: 135 MPa Grade Count:1 |
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl.. |
|||
Tensile Strength, Yield | 135 - 135 MPa @Time 1.80e+7 - 7.20e+7 sec |
19600 - 19600 psi @Time 5000 - 20000 hour |
Average value: 135 MPa Grade Count:1 |
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl.. |
|||
Tensile Strength, Yield | 135 MPa @Strain 0.200 %, Temperature 980 °C |
19600 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes Waspaloy™ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, go.. |
|||
Tensile Strength, Yield | 135 MPa @Strain 0.200 %, Temperature 980 °C |
19600 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 4031 PBT (Europe-Africa-Middle East) VALOX 4031 is a 30% high strength glass fibre reinforced PBT injection moulding resin with excellent strength, stiffness and heat resistance. Applications: appliance handles, spotlights, electric mo.. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 420 PBT (Europe-Africa-Middle East) VALOX 420 is a 30% glass fiber reinforced PBT injection moulding resin with excellent mechanical and thermal properties. Applications: appliance handles, spotlights, electric motors. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 553 PBT (Europe-Africa-Middle East) VALOX 553 is a 30% glass fibre reinforced, flame retardant PBT+PC blend with good warpage characteristics. Applications: appliance handles, spotlights, electric motors, pumphousings. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 865 PBT (Europe-Africa-Middle East) VALOX 865 is a 30% glass fibre reinforced, non blooming flame retardant PBT+PET blend with an excellent surface appearance. Applications: External housings, steam irons, appliance housings and light.. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | 50 mm/min, Injection Molded; ISO 527-2/50; ASTM D638 |
Styron DLGF9411.00 Polypropylene Overview: DLGF 9400.00 is a 40% long glass fiber reinforced grade with good flow properties. The glass fibers (12 mm length) are coupled to the polypropylene matrix resulting in high stiffness and s.. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® V8280SF PBT+PET High Modulus, PBT+PET, 40% Glass Reinforced, Mold Release, Super High Flow |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
Polyram PlusTek PA324G6 Nylon 6.6, UL-94 V-0 30% Glass Fiber Self extinguishing (UL-94 V-0) 30% glass fiber reinforced polyamide 6.6 for component with high stiffness and dimensional stabilityInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
Polyram PlusTek PA325G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant 30% glass fiber reinforced flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
Polyram Polytron P50B11 Homopolymer Polypropylene, Chemically Coupled 50% LGF A chemically coupled 50% LGF reinforced black PP, heat stabilized for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
Polyram Polytron P50N01 Homopolymer Polypropylene, Chemically Coupled 50% Long Glass Fiber A CHEMICALLY COUPLED 50% LONG GLASS FIBER REINFORCED NATURAL POLYPROPYLENE HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ISO 527 |
Polyram Polytron P50N07 Polypropylene, 50% Long Glass Fiber, UV Stabilized A chemically coupled 50% long glass fiber reinforced natural polypropylene, heat stabilized, UV stabilized for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ISO 527 |
Polyram RamSter PF306G6 PBT, 30% Glass Fiber 30% Glass fiber reinforced, low viscosity PBT for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
Polyram RamSter PE301G6 PET, 30% Glass Fiber 30% Glass-fiber reinforced, heat stabilized PET for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM D638, ISO R527 |
EPICHEM PA 6/66 GF 30 Polyamide 6/66, 30% Glass Characteristics: 30% glass fibre filled |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | 50mm/min; ISO 527-2 |
BASF Ultradur B 4300 G6 High Speed Unc. 30% Glass Filled PBT Ultradur B 4300 G6 High Speed Unc. is a high flow, fast cycling with low warpage, 30% glass filled, pigmented black, injection molding PBT for industrial parts, rigid tough and dimensional stable ap.. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R530 NAT Nylon 66, 30% Glass Reinforced, Conditioned Vydyne® R530 NAT is general-purpose, injection-molding grade, 30% glass-fiber reinforced PA66 resin. Available in natural, it is lubricated for good machine feed, flow and mold releaseAvailability:.. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | 50mm/min; ISO 527 |
BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Conditioned) Ultramid B3G8 BK00564 is a 40% glass filled, pigmented black, injection molding PA6 grade. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM D638 |
Ashley Polymers Ashlene® E126 PET Polyester, 30% Glass Reinforced PET Polyester, economy grade with 30% glass reinforcement.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | v = 50 mm/min; ISO 527-2 |
CENTROPLAST CENTRODAL GF Polyoxymethylene 30% glass fiber This material has good hot water resistance and sliding properties. Its applications include seals, scrapers and chain guides, and toothed wheels and rollers.Information provided by CENTROPLAST Eng.. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | Wet; ASTM D638 |
Asahi Kasei Leona® 14G33 33% Glass Filled Nylon 66 Enhanced strength and stiffness; with 33% GF. Superior heat aging resistance, fatigue resistance, and creep resistance.Applications:Mechanical and electrical parts, engine mounts and other under-the.. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
Polyram Polytron P50B01 Homopolymer Polypropylene, Chemically Coupled 50% LGF A chemically coupled 50% LGF reinforced black PP, heat stabilized for high temperature applications such as under the hood automotive parts.Information provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
Polyram RamTal PM3007G6 Acetal, 30% Glass Fiber 30% Glass-fiber reinforced polyacetal for injection molding applications.Information provided by Polyram Ram On Ind. |