PolyOne Nymax™ ND 1233 GF Black Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name Nymax™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Nymax™ ND 1233 GF Black Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durability in harsh environments. These materials are available in a broad range of reinforcement levels depending upon stiffness characteristics desired and have been formulated to offer ease of processing in most standard thermoplastic processing equipmentMolded Test Bars: Dry as MoldedInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 1.0 %
1.0 %
24h/23C; ISO 62
1.0 %

@Thickness 3.18 mm
1.0 %

@Thickness 0.125 in
@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield 135 MPa
19600 psi
ISO 527-2
Elongation at Break 2.0 %
2.0 %
Type I, 5.1 mm/min; ASTM D638
2.0 - 4.0 %
2.0 - 4.0 %
ISO 527-2
Flexural Strength 230 MPa
33400 psi
ASTM D790
230 MPa
33400 psi
ISO 178
Flexural Modulus 9.00 GPa
1310 ksi
ASTM D790
9.00 GPa
1310 ksi
ISO 178
Izod Impact, Notched 0.640 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
1.20 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
Peak Melting Temperature; ASTM D789
260 °C
500 °F
ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
Unannealed; ISO 75-2/A
230 °C

@Thickness 3.18 mm
446 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Mold Temperature 60.0 - 107 °C
140 - 225 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Additive Heat Stabilizer
Appearance Black
Features General Purpose
Heat Stabilized
Industrial Resin
Filler / Reinforcement Glass Fiber Reinforcement, 33% Filler by Weight
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Processing Method Injection Molding
Regional Availability North America
South America
Uses Automotive Applications
Construction Applications
Consumer Applications
General Purpose
Industrial Applications