Styron DLGF9411.00 Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Styron |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron DLGF9411.00 Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: DLGF 9400.00 is a 40% long glass fiber reinforced grade with good flow properties. The glass fibers (12 mm length) are coupled to the polypropylene matrix resulting in high stiffness and strength.Information provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792; ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 135 MPa | 19600 psi | 50 mm/min, Injection Molded; ISO 527-2/50; ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | 50 mm/min, Injection Molded; ISO 527-2/50; ASTM D638 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | Injection Molded; ASTM D638; ISO 527-2 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178; ASTM D790 |
| Flexural Modulus | 9.25 GPa | 1340 ksi | Method I (3 point load), Injection Molded; ISO 178; ASTM D790 |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | Injection Molded; ISO 179/1fU |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | Injection Molded; ISO 179/1eA |
| Multi-axial Impact @ -30°C Total Energy | 15.0 J @Thickness 3.00 mm, Temperature 23.0 °C |
11.1 ft-lb @Thickness 0.118 in, Temperature 73.4 °F |
Injection Molded, Ductile Failure; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Unannealed; ISO 75-2/A; ASTM D648 |