Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | 0.05"/min test speed; ASTM D790A |
Ineos N10N-00 Polypropylene Impact Copolymer Grade N10N-00 is a nucleated polypropylene impact copolymer with an excellent balance of stiffness and impact resistance for injection molding applications and compounding products used in Lawn and .. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM D790B |
ExxonMobil HDPE HD 6605.70 High Density Polyethylene Copolymer Resin Product Description: HD 6605.70 is a narrow molecular weight hexane copolymer designed for a wide range of injection molding applications, offering excellent ESCR with good stiffness-toughness balan.. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 159000 psi | 0.5 in/min; ASTM D790A |
ExxonMobil PP143KNE1 Polypropylene Homopolymer Product Description: A high impact copolymer resin designed consumer and industrial applications.Availability: North America Features:Good ColorabilityGood Dimensional StabilityGood Mold ReleaseGoo.. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | 0.05 in/min; ASTM D790A |
ExxonMobil PP7855E1 Polypropylene Homopolymer Product Description: A high crystallinity, medium impact strength copolymer resin with high melt flow rate and good processing attributes. It is designed for injection-molded automotive interior ap.. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM D790 |
ExxonMobil HD 6605.70 Injection Molding Resin Product Description: HD 6605.70 is a narrow molecular weight hexane copolymer designed for a wide range of injection molding applications, offering excellent ESCR with good stiffness-toughness balan.. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM D790A |
Dow R792-35RNA Polypropylene Random Copolymer Resin OverviewControlled rheology productConsistent processabilityContains clarifying additiveContains an antistatic additiveComplies with U.S. FDA 21 CFR 177.1520 (c)3.1a, Canadian HPFB No ObjectionDOW R.. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM-D790 |
Braskem GF4950HS HDPE Blow Molding Polyethylene Copolymer GF4950HS resin is a high-density polyethylene (HDPE), bimodal copolymer offering a combination of good processability and environmental stress crack resistance (ESCR). It is thus recommended for the.. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM D790A |
Braskem H 203 Fiber Extrusion Polypropylene Homopolymer Continuous filaments for carpets, sewing yarns and ropes; Staple fibers for rugs and blankets; Nonwovens by thermobonded process.Information provided by Braskem. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM-D790 |
Braskem PCD 0140 HECO Polypropylene Heterophasic Copolymer PCD 0140 is a low melt flow rate heterophasic copolymer with high impact resistance. This resin was developed for steel pipe coating extrusion. PCD 0140 is highly protected against thermal aging and.. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM-D790 |
Braskem PCD 0140BR HECO Polypropylene Heterophasic Copolymer PCD 0140BR is a low melt flow rate heterophasic copolymer with high impact resistance. This resin was developed for steel pipe coating extrusion. PCD 0140BR is highly protected against thermal aging.. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM-D790 |
Braskem H 203 HOMO Polypropylene Homopolymer H 203 is a high melt flow rate homopolymer with a general purpose additive package. This product exhibits excellent processability and good stiffness/impact strength balance. It also features a low .. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM-D790 |
Braskem HB0454HR HDPE Blow Molding Polyethylene Copolymer HB0454HR is a high-density polyethylene copolymer resin with average molecular weight produced by the Unipol® process. A bottle made with HB0454HR shows excellent processability, color, and superfi.. |
|||
Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM-D790 |
Braskem CP 284R HECO Polypropylene Heterophasic Copolymer CP 284R is a heterophasic copolymer designed for injection molding of pails and containers with excellent stiffness/impact strength balance. This resin also exhibits excellent productivity and proce.. |