LATI Latamid 12 G/50 PA 12, 50% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 50% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 12 G/50 PA 12, 50% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 12 (PA12) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0055 cm/cm
0.0035 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.010 cm/cm
0.0075 - 0.010 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa

@Temperature 150 °C
 7980 psi

@Temperature 302 °F
80.0 MPa

@Temperature 120 °C
 11600 psi

@Temperature 248 °F
90.0 MPa

@Temperature 90.0 °C
 13100 psi

@Temperature 194 °F
110 MPa

@Temperature 60.0 °C
 16000 psi

@Temperature 140 °F
150 MPa

@Temperature 23.0 °C
 21800 psi

@Temperature 73.4 °F
Elongation at Break 4.5 %

@Temperature 23.0 °C
 4.5 %

@Temperature 73.4 °F
6.2 %

@Temperature 60.0 °C
 6.2 %

@Temperature 140 °F
6.7 %

@Temperature 90.0 °C
 6.7 %

@Temperature 194 °F
7.7 %

@Temperature 120 °C
 7.7 %

@Temperature 248 °F
8.6 %

@Temperature 150 °C
 8.6 %

@Temperature 302 °F
Elongation at Yield 6.0 %

@Temperature 23.0 °C
 6.0 %

@Temperature 73.4 °F
Tensile Modulus 3.30 GPa

@Temperature 150 °C
 479 ksi

@Temperature 302 °F
4.30 GPa

@Temperature 120 °C
 624 ksi

@Temperature 248 °F
5.10 GPa

@Temperature 90.0 °C
 740 ksi

@Temperature 194 °F
6.30 GPa

@Temperature 60.0 °C
 914 ksi

@Temperature 140 °F
10.5 GPa

@Temperature 23.0 °C
 1520 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 10.0 J/cm²
47.6 ft-lb/in²
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Vicat Softening Point 180 °C

@Load 5.00 kg
 356 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 220 - 240 °C
428 - 464 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 70.0 - 90.0 °C

@Time 10800 sec
 158 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa