Victrex® PEEK 90GL60 Polyetheretherketone, 60% Glass Fibre Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer Victrex
Trade Name PEEK
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 90GL60 Polyetheretherketone, 60% Glass Fibre Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description:High performance thermoplastic material, 60% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact compliant, colour natural/beige.Typical Application Areas:Applications where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®
Physical Properties Metric English Comments
Density 1.83 g/cc
0.0661 lb/in³
Crystalline; ISO 1183
Water Absorption at Saturation 0.40 %

@Temperature 23.0 °C
0.40 %

@Temperature 73.4 °F
Equilibrium; by immersion; ISO 62-1
Viscosity 525000 cP

@Temperature 400 °C
525000 cP

@Temperature 752 °F
melt; ISO 11443
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
380°C nozzle, 190°C tool; ISO 294-4
Spiral Flow 10.0 cm

@Thickness 1.00 mm
3.94 in

@Thickness 0.0394 in
380°C nozzle, 190°C tool
Mechanical Properties Metric English Comments
Hardness, Shore D 87

@Temperature 23.0 °C
87

@Temperature 73.4 °F
ISO 868
Tensile Strength at Break 50.0 MPa

@Temperature 275 °C
7250 psi

@Temperature 527 °F
ISO 527
90.0 MPa

@Temperature 175 °C
13100 psi

@Temperature 347 °F
ISO 527
150 MPa

@Temperature 125 °C
21800 psi

@Temperature 257 °F
ISO 527
240 MPa

@Temperature 23.0 °C
34800 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 1.5 %

@Temperature 23.0 °C
1.5 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 25.0 GPa

@Temperature 23.0 °C
3630 ksi

@Temperature 73.4 °F
ISO 527
Flexural Strength 360 MPa

@Temperature 23.0 °C
52200 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 23.5 GPa

@Temperature 23.0 °C
3410 ksi

@Temperature 73.4 °F
ISO 178
Compressive Strength 65.0 MPa

@Temperature 200 °C
9430 psi

@Temperature 392 °F
ISO 604
140 MPa

@Temperature 120 °C
20300 psi

@Temperature 248 °F
ISO 604
230 MPa

@Temperature 23.0 °C
33400 psi

@Temperature 73.4 °F
ISO 604
Izod Impact, Notched (ISO) 11.5 kJ/m²

@Temperature 23.0 °C
5.47 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
ISO 180/U
Thermal Properties Metric English Comments
CTE, linear 30.0 µm/m-°C

@Temperature <=143 °C
16.7 µin/in-°F

@Temperature <=289 °F
Average below Tg; ISO 11359
70.0 µm/m-°C

@Temperature >=143 °C
38.9 µin/in-°F

@Temperature >=289 °F
Average above Tg; ISO 11359
CTE, linear, Parallel to Flow 13.0 µm/m-°C

@Temperature <=143 °C
7.22 µin/in-°F

@Temperature <=289 °F
Below Tg; ISO 11359
15.0 µm/m-°C

@Temperature >=143 °C
8.33 µin/in-°F

@Temperature >=289 °F
Above Tg; ISO 11359
Thermal Conductivity 0.550 W/m-K

@Temperature 23.0 °C
3.82 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
ISO/CD 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 343 °C
649 °F
ISO 75A-f
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Dielectric Constant 3.8

@Frequency 1000 Hz,
Temperature 23.0 °C
3.8

@Frequency 1000 Hz,
Temperature 73.4 °F
IEC 60250
Dielectric Strength 22.0 kV/mm

@Thickness 2.50 mm
559 kV/in

@Thickness 0.0984 in
IEC 60243-1
Dissipation Factor 0.0040

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
0.0040

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
IEC 60250
Comparative Tracking Index 150 V
150 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 380 °C
716 °F
Mold Temperature 180 - 210 °C
356 - 410 °F
Drying Temperature 120 °C

@Time 18000 sec
248 °F

@Time 5.00 hour
150 °C

@Time 10800 sec
302 °F

@Time 3.00 hour