LATI Larpeek 10 G/50 PEEK, 50% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer LATI
Trade Name Larpeek
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larpeek 10 G/50 PEEK, 50% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyetheretherketone (PEEK) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.73 g/cc
0.0625 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0040 cm/cm
0.0015 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0040 - 0.0065 cm/cm
0.0040 - 0.0065 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa

@Temperature 150 °C
 21800 psi

@Temperature 302 °F
170 MPa

@Temperature 120 °C
 24700 psi

@Temperature 248 °F
195 MPa

@Temperature 90.0 °C
 28300 psi

@Temperature 194 °F
210 MPa

@Temperature 60.0 °C
 30500 psi

@Temperature 140 °F
220 MPa

@Temperature 23.0 °C
 31900 psi

@Temperature 73.4 °F
Elongation at Break 1.8 %

@Temperature 23.0 °C
 1.8 %

@Temperature 73.4 °F
1.8 %

@Temperature 60.0 °C
 1.8 %

@Temperature 140 °F
1.8 %

@Temperature 90.0 °C
 1.8 %

@Temperature 194 °F
1.9 %

@Temperature 120 °C
 1.9 %

@Temperature 248 °F
1.9 %

@Temperature 150 °C
 1.9 %

@Temperature 302 °F
Tensile Modulus 16.6 GPa

@Temperature 150 °C
 2410 ksi

@Temperature 302 °F
17.0 GPa

@Temperature 120 °C
 2470 ksi

@Temperature 248 °F
17.5 GPa

@Temperature 90.0 °C
 2540 ksi

@Temperature 194 °F
17.8 GPa

@Temperature 60.0 °C
 2580 ksi

@Temperature 140 °F
18.0 GPa

@Temperature 23.0 °C
 2610 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 240 °C
464 °F
Deflection Temperature at 0.46 MPa (66 psi) >= 300 °C
>= 572 °F
Deflection Temperature at 1.8 MPa (264 psi) >= 300 °C
>= 572 °F
Vicat Softening Point >= 300 °C

@Load 5.00 kg
 >= 572 °F

@Load 11.0 lb
Flammability, UL94 V-1

@Thickness 0.750 mm
 V-1

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Glow Wire Test 875 °C

@Thickness 1.00 mm
 1610 °F

@Thickness 0.0394 in
 GWIT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Processing Properties Metric English Comments
Melt Temperature 370 - 400 °C
698 - 752 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 - 150 °C

@Time 10800 sec
 248 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa