Denka MALECCA K-600 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Denka
Trade Name MALECCA
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Denka MALECCA K-600 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had defects in terms of moldability, thermal stability, and impact resistance.ApplicationsMobile phonesvehicle-mounted audio equipmentautomotive interior componentshome electric appliancesOA equipment, etc.
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ASTM D792
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Melt Flow 15 g/10 min

@Load 10.0 kg,
Temperature 265 °C
15 g/10 min

@Load 22.0 lb,
Temperature 509 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 111
111
ISO 2039-2
117
117
ASTM D785
Tensile Strength at Break 37.0 MPa
5370 psi
50mm/min; ISO 527-2
39.0 MPa
5660 psi
ASTM D638
Tensile Strength, Yield 37.0 MPa
5370 psi
ISO 527-2
Elongation at Break 26 %
26 %
ISO 527-2
Tensile Modulus 2.10 GPa
305 ksi
1mm/min; ISO 527-1
Flexural Strength 64.0 MPa
9280 psi
15mm/min; ASTM D790
67.0 MPa
9720 psi
ISO 178
Flexural Modulus 1.95 GPa
283 ksi
15mm/min; ASTM D790
2.05 GPa
297 ksi
2mm/min; ISO 178
Izod Impact, Notched 1.46 J/cm

@Temperature 23.0 °C
2.74 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
ISO 179-2
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 112 °C
234 °F
ISO 75-2
122 °C
252 °F
ASTM D648
Vicat Softening Point 133 °C
271 °F
50N; ISO 306
Flammability, UL94 HB
HB