SABIC Innovative Plastics LNP Stat-loy W3000 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-loy W3000 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-LOY* W3000 is a compound based on Polybutylene Terephalate resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D 792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 1.09 % | 1.09 % | 23°C / 50% RH; ISO 62 |
| 0.65 % @Time 86400 sec |
0.65 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0174 cm/cm @Time 86400 sec |
0.0174 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0199 cm/cm @Time 86400 sec |
0.0199 in/in @Time 24.0 hour |
ISO 294 |
| 0.020 cm/cm @Time 86400 sec |
0.020 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
| 40.0 MPa | 5800 psi | ASTM D 638 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ISO 527 |
| 41.0 MPa | 5950 psi | ASTM D 638 | |
| Elongation at Break | 12.7 % | 12.7 % | ISO 527 |
| 14.6 % | 14.6 % | ASTM D 638 | |
| Elongation at Yield | 8.2 % | 8.2 % | ASTM D 638 |
| 10.9 % | 10.9 % | ISO 527 | |
| Tensile Modulus | 1.58 GPa | 229 ksi | 50 mm/min; ASTM D 638 |
| 1.63 GPa | 236 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| 59.0 MPa | 8560 psi | ASTM D 790 | |
| Flexural Modulus | 1.64 GPa | 238 ksi | ISO 178 |
| 1.72 GPa | 249 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.580 J/cm @Temperature 23.0 °C |
1.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 12.54 J/cm @Temperature 23.0 °C |
23.49 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 137 kJ/m² @Temperature 23.0 °C |
65.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 32.0 J @Temperature 23.0 °C |
23.6 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C @Thickness 3.20 mm |
115 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D 257 |