SABIC Innovative Plastics LNP THERMOTUF MX00619 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF MX00619 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* MX00619 is a compound based on Polypropylene resin containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| Tensile Modulus | 3.137 GPa | 455.0 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 2.81 GPa | 408 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.36 J/cm | 6.29 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Master Bond EP46HT-2Med Two Component Heat Resistant Biocompatible Epoxy System
- A. Schulman POLYPUR™ FPU 1185 Thermoplastic Polyurethane Compound
- A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene
- A. Schulman POLYBATCH™ Green 3012E Concentrate Based In Polyethylene
- Zylog Hipolyene® 8015 FRC Thermoplastic Polyolefin & PP Compound
- Eagle Brass 715 Copper Nickel 30%, Hard
- Bulk Molding Compounds BMC 304 Automotive Grade Molding Compound
- Arlon 44602M020 0.020" (0.508 mm) Cured Silicone Rubber with Fiberglass Substrate
- Potters Industries A-Series A-120 Soda-Lime Silica Technical Quality Solid Glass Spheres
Copyright © lookpolymers.com All Rights Reserved