Denka CL-430 Transparent Resin Polymer (MABS) ABS

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	Denka
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Denka CL-430 Transparent Resin Polymer (MABS) ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

"TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a good balance of transparency, strength and fluidity (methyl methacrylate butadiene styrene), "TE Series/CL Series," transparent ABS resins with excellent color attributes and tensile strength are available (among others).ApplicationsTX is used for:flat display substratesoptical componentsmiscellaneous goods.TP/TH are used for:food package sheeting as well as in manufacturingelectronic equipment and componentsmiscellaneous goodsTE/CL are for:electronic equipment and componentsinformation equipment componentsAV equipment, etc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	ASTM D792
Density	1.08 g/cc	0.0390 lb/in³	ISO 1183
Melt Flow	2.7 g/10 min @Load 5.00 kg, Temperature 200 °C	2.7 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133
	34 g/10 min @Load 10.0 kg, Temperature 220 °C	34 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	31	31	ISO 2039-2
Tensile Strength at Break	31.0 MPa	4500 psi	50mm/min; ISO 527-2
	37.0 MPa	5370 psi	50mm/min; ASTM D638
Elongation at Break	40 %	40 %	50mm/min; ISO 527-2
Tensile Modulus	4.20 GPa	609 ksi	50mm/min; ISO 527-1
Flexural Strength	62.0 MPa	8990 psi	ISO 178
	63.0 MPa	9140 psi	2mm/min; ASTM D790
Flexural Modulus	2.00 GPa	290 ksi	2mm/min; ISO 178
	2.01 GPa	292 ksi	2mm/min; ASTM D790
Izod Impact Resistance	16.0 J/cm²	76.1 ft-lb/in²
Charpy Impact, Notched	1.40 J/cm²	6.66 ft-lb/in²	ISO 179-2

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	64.0 °C	147 °F	ISO 75-2
	72.0 °C	162 °F	ASTM D648
Vicat Softening Point	80.0 °C	176 °F	50N; ISO 306
Flammability, UL94	HB	HB

Optical Properties	Metric	English	Comments
Haze	2.0 % @Thickness 2.00 mm	2.0 % @Thickness 0.0787 in	ISO 14782
Transmission, Visible	91 % @Thickness 2.00 mm	91 % @Thickness 0.0787 in	ISO 13468-1