SABIC Innovative Plastics NORYL WCV072 PPE+PP (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL WCV072 PPE+PP (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. Designed for evaluation in applications requiring ISO6722. 72 Shore D hardness. Processed using standard extrusion equipment.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc
1.03 g/cc
ASTM D792
Density 1.03 g/cc
0.0372 lb/in³
ISO 1183
Moisture Absorption 0.0500 %
0.0500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.12 %
0.12 %
ISO 62
Melt Flow 13.8 g/10 min

@Load 5.00 kg,
Temperature 280 °C
13.8 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 13 g/10 min

@Load 5.00 kg,
Temperature 280 °C
13 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.0 MPa
5950 psi
Type I, 50 mm/min; ASTM D638
42.0 MPa
6090 psi
50 mm/min; ISO 527
Tensile Strength, Yield 43.0 MPa
6240 psi
Type I, 50 mm/min; ASTM D638
44.0 MPa
6380 psi
50 mm/min; ISO 527
Elongation at Break 46 %
46 %
50 mm/min; ISO 527
83 %
83 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 11 %
11 %
50 mm/min; ISO 527
15 %
15 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.71 GPa
248 ksi
50 mm/min; ASTM D638
1.75 GPa
254 ksi
1 mm/min; ISO 527
Flexural Yield Strength 53.0 MPa
7690 psi
1.3 mm/min, 50 mm span; ASTM D790
59.0 MPa
8560 psi
2 mm/min; ISO 178
Flexural Modulus 1.55 GPa
225 ksi
1.3 mm/min, 50 mm span; ASTM D790
1.74 GPa
252 ksi
2 mm/min; ISO 178
Izod Impact, Notched 3.09 J/cm
5.79 ft-lb/in
ASTM D256
0.670 J/cm

@Temperature -30.0 °C
1.26 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 36.0 kJ/m²
17.1 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 3.30 J/cm²
15.7 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 45.0 J

@Temperature 23.0 °C
33.2 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 84.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 105 µm/m-°C

@Temperature -40.0 - 40.0 °C
58.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
111 µm/m-°C

@Temperature -40.0 - 40.0 °C
61.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
92.0 °C

@Thickness 3.20 mm
198 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 114 °C
237 °F
Rate B/50; ASTM D1525
114 °C
237 °F
Rate B/50; ISO 306
117 °C
243 °F
Rate B/120; ISO 306