SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ASTM D792
1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption 2.00 %
2.00 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ASTM D955
0.0093 cm/cm

@Time 86400 sec
0.0093 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D955
0.010 cm/cm

@Time 86400 sec
0.010 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
ASTM D638
42.0 MPa
6090 psi
Type I, 5 mm/min; ASTM D638
42.0 MPa
6090 psi
ISO 527
42.0 MPa
6090 psi
5 mm/min; ISO 527
Tensile Strength, Yield 42.0 MPa
6090 psi
ASTM D638
43.0 MPa
6240 psi
Type I, 5 mm/min; ASTM D638
43.0 MPa
6240 psi
ISO 527
43.0 MPa
6240 psi
5 mm/min; ISO 527
Elongation at Break 1.8 %
1.8 %
ISO 527
1.9 %
1.9 %
5 mm/min; ISO 527
1.9 %
1.9 %
ASTM D638
2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 1.8 %
1.8 %
ASTM D638
1.8 %
1.8 %
Type I, 5 mm/min; ASTM D638
1.8 %
1.8 %
ISO 527
1.8 %
1.8 %
5 mm/min; ISO 527
Tensile Modulus 3.62 GPa
525 ksi
1 mm/min; ISO 527
4.13 GPa
599 ksi
50 mm/min; ASTM D638
Flexural Strength 55.0 MPa
7980 psi
ASTM D790
59.0 MPa
8560 psi
1.3 mm/min, 50 mm span; ASTM D790
61.0 MPa
8850 psi
ISO 178
Flexural Yield Strength 61.0 MPa
8850 psi
2 mm/min; ISO 178
Flexural Modulus 3.20 GPa
464 ksi
ISO 178
3.20 GPa
464 ksi
2 mm/min; ISO 178
3.44 GPa
499 ksi
ASTM D790
3.45 GPa
500 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.24 J/cm
4.20 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J
2.95 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 93.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
94.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
94.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
52.2 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 61.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
62.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
62.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
34.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
96.0 °C

@Thickness 3.20 mm
205 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
87.0 °C

@Thickness 3.20 mm
189 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
Electrical Properties Metric English Comments
Surface Resistance 10 - 1000 ohm
10 - 1000 ohm
ASTM D257