Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 41.0 MPa @Temperature 23.0 °C |
5950 psi @Temperature 73.4 °F |
ISO 527 (1BA bar) |
DuPont Performance Polymers Hytrel® 6359FG NC010 TPC-ET
(Unverified Data**) Hytrel® 6359FG is a medium modulus Hytrel® grade with nominal durometer hardness of 63D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processing t.. |
|||
Tensile Strength at Break | 41.0 MPa @Temperature 23.0 °C |
5950 psi @Temperature 73.4 °F |
ISO 527 (1BA bar) |
DuPont Performance Polymers Hytrel® HTR8730 BK320 TPC-ET
(Unverified Data**) Hytrel® HTR8730 BK320 is a high viscosity thermoplastic polyester elastomer designed for blow molding. It has excellent mechanical properties at elevated temperatures and very good resistance to mo.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO R 527 |
Fainplast Compounds RKS 205/K Rigid PVC, Antishock Extrusion Lead Free Metal effect antishock profiles |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO R 527 |
Fainplast Compounds RST 0447/1 Rigid PVC, Extrusion Lead Free Extrusion transparent films |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | DIN 53504 |
Huntsman IROGRAN® A 95 E 4813 Polyester-Based TPU-High Performance Grade Introduction: IROGRAN A 95 R 4813 is a thermoplastic polyester- polyurethane for injection moulding applications. Additional characteristics of the product are very short cycle times and high dimens.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
Ineos Styrenics 166H General Purpose Polystyrene (NAFTA) Description: Polystyrene 166H is a high molecular weight general purpose polystyrene with good flow and crystal clarity. Polystyrene 166H offers good processing characteristics while yielding parts .. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP HH0420A PA11 LNP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP HX00059 PA11 (Europe-Africa-Middle East) LNP * Lubricomp * HX00059 is a compound based on PA 11 resin, containing a Proprietary Lubricant. Added features include: Internally Lubricated. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCV072 PPE+PP (Europe-Africa-Middle East) Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics PREVEX VGAX PPE+PS Improved productivity and reliability. Nonchlorinated, nonbrominated flame retardant. 180F HDT. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp RP0049 PA 66 LNP LUBRICOMP* RP0049 is a compound based on Nylon 66 resin containing Flame Retardant, PTFE, Silicone. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP f.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon CX01039 PS (Europe-Africa-Middle East) LNP* Stat-kon* CX01039 is a compound based on Polystyrene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ357 PBT+PC (Asia Pacific) Valox* Resin IQ357: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® IQ357 PBT+PC (Europe-Africa-Middle East) Valox* Resin IQ357: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ357U PBT+PC Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ357U PBT+PC (Asia Pacific) Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xenoy® CL402 PBT+PC (Europe-Africa-Middle East) XENOY CL402 is a high viscosity, unfilled, elastomer modified PC/PBT blend for extrusion/blowmolding applications. ISO1043-label: PC+PBT-I.This data was supplied by SABIC-IP for the Europe-Africa-Mi.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP HB006 PA11 LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing 30% Glass Bead. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp PH0700B PA 6 LNP* Thermocomp* PH0700B is a Nylon 6 base resin containing Tungsten. Characteristics are High Specific Gravity.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP V1000SU PA LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® V3903WX PBT+PC (Asia Pacific) Unreinforced fllame retardant PBT/PC blends with good chemical resistance and low temperature impact, UV stablized |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY W3000XXJ PBT LNP* STAT-LOY* W3000XXJ is a compound based on PBT. Added features of this grade include: Anti-Stat, Colorable, Healthcare |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | 50mm/min; ISO 527-2 |
Denka MALECCA K-510 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
Diapolyacrylate Shinko-Lac® U400B Transparent ABS Shinko-Lac® is a registered trademark of Diapolyacrylate Company Limited. Information provided by Dayson Polymers. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO R 527 |
Fainplast Compounds R 218 Rigid PVC, Extrusion Shutters and shiny profiles |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
Toyobo PELPRENE™ S3002 Polyester TPE, Ultra Heat-resistant Features: Polyester TPE, Ultra Heat-resistantInformation provided by Toyobo. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | Type 1, 2"/min; ASTM D638 |
Proto3000 PC-ABS Fused Deposition Modeling Polymer Description: PC-ABS (polycarbonate-ABS) is one of the most widely used industrial thermoplastics. PC-ABS offers the most desirable properties of both materials - the superior strength and heat resis.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HFD4471 PC Lexan* HFD4471 is a 10% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4417 has enhanced mold release, impact ductili.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HFD4471 PC (Asia Pacific) Lexan* HFD4471 is a 10% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4417 has enhanced mold release, impact ductili.. |
|||
Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON ME003S PP (Asia Pacific) LNP STAT-KON* ME003S is a compound based on Polypropylene resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |