SABIC Innovative Plastics LNP STAT-LOY W3000XXJ PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY W3000XXJ PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-LOY* W3000XXJ is a compound based on PBT. Added features of this grade include: Anti-Stat, Colorable, Healthcare
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.230 % | 0.230 % | 50% RH, 24 hrs; ASTM D570 |
| 0.370 % | 0.370 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| 42.0 MPa | 6090 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.3 % | 4.3 % | Type I, 5 mm/min; ASTM D638 |
| 9.6 % | 9.6 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 8.5 % | 8.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.88 GPa | 273 ksi | 1 mm/min; ISO 527 |
| 1.93 GPa | 280 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
| Flexural Modulus | 1.89 GPa | 274 ksi | 2 mm/min; ISO 178 |
| 1.94 GPa | 281 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.610 J/cm | 1.14 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.0 J/cm | 26.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 89.0 kJ/m² | 42.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 115 µm/m-°C @Temperature -30.0 - 30.0 °C |
63.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 128 µm/m-°C @Temperature -30.0 - 30.0 °C |
71.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+11 - 1.00e+13 ohm | 1.00e+11 - 1.00e+13 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Schwartz Technical Plastics LAMIGAMID® 317 Cast Polyamide 6, Heat Stabilized, Dry
- Suzhou Hipro Polymers Hiprolon® 200 MC HLS G30 Nylon 1010, 30% glass fiber filled
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- DuPont Elvanol® T-25 Polyvinyl Alcohol Textile Grade
- Covestro Makrolon® 6557 Polycarbonate, Injection Grade
- ELM® SoyFluid™ Hydraulic All Season Premium Biodegradable - Biobased Hydraulic Oil
- BCC Products BC 6126 Epoxy Surface Coat/Casting
- Bhansali Engineering Abstron AN-312 Flame Retardant ABS Grade
Copyright © lookpolymers.com All Rights Reserved