| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Hytrel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Hytrel® DYM1300 BK320 TPC-ET
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hytrel® DYM1300 is a high performance thermoplastic elastomer with high modulus, suited for air bag door applications.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 2.00 mm |
0.015 in/in @Thickness 0.0787 in |
Parallel |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 240 °C |
14 g/10 min @Load 4.76 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 @Time 15.0 sec |
65 @Time 0.00417 hour |
ISO 868 |
| Tensile Strength at Break | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
ISO 527 (1BA bar) |
| Tensile Stress | 30.0 MPa @Strain 10.0 %, Temperature 23.0 °C |
4350 psi @Strain 10.0 %, Temperature 73.4 °F |
ISO 527 (1BA bar) |
| Elongation at Break | 250 % @Temperature 23.0 °C |
250 % @Temperature 73.4 °F |
ISO 527 (1BA bar) |
| Tensile Modulus | 1.35 GPa @Temperature 23.0 °C |
196 ksi @Temperature 73.4 °F |
ISO 527 |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 245 °C | 473 °F | Optimum; Injection Molding |
| 240 - 250 °C | 464 - 482 °F | Injection Molding | |
| Mold Temperature | 45.0 °C | 113 °F | optimum; Injection Molding |
| <= 55.0 °C | <= 131 °F | Injection Molding | |
| Drying Temperature | 110 °C | 230 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Moisture Content | <= 0.050 % | <= 0.050 % | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black Color | |
| Forms | Pellets | |
| Generic | TPC-ET+PBT | |
| Material Status | Preliminary Data | |
| Part Marking Code | >TPC-ET+PBT< | ISO 11469 |
| Processing Method | Injection Molding | |
| Product Category | Air Bag Door Resins | |
| Region Available - Global | Yes | |
| Resin Identification | TPC-ET+PBT | ISO 1043 |
| RoHS Compliance | Contact Manufacturer |
Users viewing this material also viewed the following:
- MV Labs SR200 SrBr2 Strontium bromide
- Polimeri Europa KOBLEND HI 10 PBT+PC, Impact Grade (discontinued **)
- LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**)
- LTL Color Compounds ColorFast® ACR100 Polymethylmethacrylate
- Plenco 7500 Phenolic, Granular, Compression Molded
- A. Schulman CP814-01 Linear, Low-Density Polyethylene
- Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- ExxonMobil LLDPE LL 6201XR Molding Linear Low Density Polyethylene Resin (European Grade)
- ArcelorMittal Save 30-15 Electrical Steel
Copyright © lookpolymers.com All Rights Reserved