Huntsman IROGRAN® A 70 E 4675 Polyester-Based TPU-High Performance Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 70 E 4675 Polyester-Based TPU-High Performance Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 70 E 4675 is a softener free thermoplastic special-polyester-polyurethane for injection molding applications. Additional characteristics of the product are very short cycle times and high dimensional stabilityPerformance Features: Easy demolding High demolding stability Short cycle times Softener-free High elasticity Applications: For the production of casual shoe soles, cable bushings, plugs, buffers.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.025 cm/cm | 0.025 in/in | ASTM D995 |
| Melt Index of Compound | 30 g/10 min @Load 21.6 kg, Temperature 190 °C |
30 g/10 min @Load 47.6 lb, Temperature 374 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | ASTM D2240 |
| Hardness, Shore D | 25 | 25 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | DIN 53504 |
| Elongation at Break | 650 % | 650 % | ASTM D412 |
| 100% Modulus | 0.00330 GPa | 0.479 ksi | DIN 53504 |
| 300% Modulus | 0.00580 GPa | 0.841 ksi | DIN 53504 |
| Rebound | 25 % | 25 % | Bayshore; ASTM D2632 |
| Tear Strength | 52.6 kN/m | 300 pli | ASTM D624 |
| Abrasion | 80 | 80 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 35 % @Temperature 23.0 °C, Time 252000 sec |
35 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 58 % @Temperature 70.0 °C, Time 86400 sec |
58 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 125 - 190 °C | 257 - 374 °F | Huntsman/TMA |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-30-20 Cellular Urethane Foam
- SABIC Innovative Plastics LNP LUBRICOMP DFL14 PC
- DSM Akulon® Ultraflow™ K-FHGM44 Nylon 6-40% Glass and Mineral Reinforced (European and Asian Grade) (Cond) (d
- Hexion Bakelite™ X22 Phenolic Formaldehyde Resin, UL Listed (discontinued **)
- Ineos ABS Lustran® H606 LS
- Styron CALIBREâ„¢ MEGARAD 2081-22 Polycarbonate Resin
- Vyncolit 4451 XB Novolac Phenolic
- Loctite® 363 Acrylic Light Cure Adhesive
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 40 PHR N220 (ISAF) Filler
- ExxonMobil PP7815E1 Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved