Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Mineral Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifically to be cost effective for most applications requiring high stiffness, good dimensional stability and chemical resistance. Typical applications for Amodel AS-1566 HS resin include electrical connectors and housings, motor components, pistons, covers, engine parts and transmission components. - Black: AS-1566 HS BK 324 - Black: AS-1566 HS BK 545 - Natural: AS-1566 HS NTData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.84 g/cc
0.0665 lb/in³
ISO 1183/A
Filler Content 65 %
65 %
GlassMineral
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 207 MPa
30000 psi
ASTM D638
43.4 MPa

@Temperature 175 °C
6290 psi

@Temperature 347 °F
ISO 527-2
52.4 MPa

@Temperature 150 °C
7600 psi

@Temperature 302 °F
ISO 527-2
127 MPa

@Temperature 100 °C
18400 psi

@Temperature 212 °F
ISO 527-2
200 MPa

@Temperature 23.0 °C
29000 psi

@Temperature 73.4 °F
ISO 527-2
Tensile Strength 175 MPa
25400 psi
Conditioned; ASTM D638
Elongation at Break 1.7 %
1.7 %
ASTM D638
1.8 %
1.8 %
Conditioned; ASTM D638
1.4 %

@Temperature 23.0 °C
1.4 %

@Temperature 73.4 °F
ISO 527-2
1.5 %

@Temperature 100 °C
1.5 %

@Temperature 212 °F
ISO 527-2
3.1 %

@Temperature 175 °C
3.1 %

@Temperature 347 °F
ISO 527-2
3.4 %

@Temperature 150 °C
3.4 %

@Temperature 302 °F
ISO 527-2
Tensile Modulus 20.0 GPa
2900 ksi
ASTM D638
20.9 GPa
3030 ksi
Conditioned; ASTM D638
6.21 GPa

@Temperature 175 °C
901 ksi

@Temperature 347 °F
ISO 527-2
7.31 GPa

@Temperature 150 °C
1060 ksi

@Temperature 302 °F
ISO 527-2
17.2 GPa

@Temperature 100 °C
2490 ksi

@Temperature 212 °F
ISO 527-2
22.5 GPa

@Temperature 23.0 °C
3260 ksi

@Temperature 73.4 °F
ISO 527-2
Flexural Strength 263 MPa
38100 psi
Conditioned; ASTM D790
75.8 MPa

@Temperature 175 °C
11000 psi

@Temperature 347 °F
ISO 178
95.8 MPa

@Temperature 150 °C
13900 psi

@Temperature 302 °F
ISO 178
205 MPa

@Temperature 100 °C
29700 psi

@Temperature 212 °F
ISO 178
284 MPa

@Temperature 23.0 °C
41200 psi

@Temperature 73.4 °F
ISO 178
Flexural Yield Strength 290 MPa
42100 psi
ASTM D790
Flexural Modulus 18.6 GPa
2700 ksi
ASTM D790
19.9 GPa
2890 ksi
Conditioned; ASTM D790
6.41 GPa

@Temperature 175 °C
930 ksi

@Temperature 347 °F
ISO 178
7.31 GPa

@Temperature 150 °C
1060 ksi

@Temperature 302 °F
ISO 178
16.8 GPa

@Temperature 100 °C
2440 ksi

@Temperature 212 °F
ISO 178
20.5 GPa

@Temperature 23.0 °C
2970 ksi

@Temperature 73.4 °F
ISO 178
Shear Strength 62.7 MPa
9090 psi
Conditioned; ASTM D732
80.0 MPa
11600 psi
ASTM D732
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
Conditioned; ASTM D256
0.640 J/cm
1.20 ft-lb/in
ASTM D256
5.90 J/cm
11.1 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 6.50 kJ/m²
3.09 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 44.0 kJ/m²

@Temperature 23.0 °C
20.9 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 3.40 J/cm²
16.2 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.610 J/cm²
2.90 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 17.0 µm/m-°C

@Temperature 0.000 - 100 °C
9.44 µin/in-°F

@Temperature 32.0 - 212 °F
TMA; ASTM E831
17.0 µm/m-°C

@Temperature 100 - 200 °C
9.44 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 40.0 µm/m-°C

@Temperature 0.000 - 100 °C
22.2 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E831
72.0 µm/m-°C

@Temperature 100 - 200 °C
40.0 µin/in-°F

@Temperature 212 - 392 °F
ASTM E831
Melting Point 311 °C
592 °F
Peak; ASTM D3418
311 °C
592 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 278 °C
532 °F
Annealed; ASTM D648
280 °C
536 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Feed Temperature 79.4 °C
175 °F
Hopper Temperature
Rear Barrel Temperature 307 - 329 °C
585 - 624 °F
Front Barrel Temperature 307 - 329 °C
585 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 65.6 - 166 °C
150 - 331 °F
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.045 %
0.045 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Appearance Black
Natural Color
Automotive Specifications ASTM D4000 PA122 R65 Color: BK324 Black
ASTM D4000 PA122 R65 Color: NT Natural
ASTM D6779 PA122R65
DELPHI DCM4899 Color: BK324 Black
DELPHI DCM4899 Color: NT Natural
DELPHI M-2987 Color: BK324 Black
DELPHI M-2987 Color: NT Natural
DELPHI M-53292
DELPHI M-53292 Color: BK545 Black
GM GM7001M PA6T/6I/66 A3 A22 A42 A64 BJ721 DE1830 KS1750 Color: NT Natural
GM GMP.PPA.003 Color: BK324 Black
ISO 1874 PA6T/6I/66, MH, 11-120, (GF+MD)64 Color: BK324 Black
ISO 1874 PA6T/6I/66, MH, 11-120, (GF+MD)64 Color: NT Natural
TRW SP-13161601 Color: BK324 Black
TRW SP-13161601 Color: NT Natural
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Toughness
Heat Stabilized
High Heat Resistance
High Strength
Low CLTE
Ultra High Stiffness
Forms Pellets
Generic PPA
Processing Method Injection Molding
RoHS Compliance RoHS Compliant
Uses Automotive Applications
Automotive Electronics
Automotive Under the Hood