Solvay Specialty Polymers Primef® 4010 Polyphenylene Sulfide (PPS), 40% Glass Fiber Reinforcement  (discontinu

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Primef® 4010 Polyphenylene Sulfide (PPS), 40% Glass Fiber Reinforcement  (discontinu.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Primef 4010 is a 40% glass fiber reinforced polyphenylene sulfide (PPS) that offers enhanced mechanical properties. In general, PPS offers an excellent balance of properties including high temperature resistance, chemical resistance, dimensional stability and electrical characteristics. Because of its inherent flame retardancy, PPS is a good choice for high-temperature electrical and electronic applications.Features: Flame Retardant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Processability; Good Strength; High Flow; High Heat Resistance; Low to No Water AbsorptionUses: Availability: EuropeHolding Time: 3 secCooling Time, 2 mm: 2.5 secInformation provide by Solvay Specialty Polymers
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 180 MPa

@Temperature 23.0 °C
26100 psi

@Temperature 73.4 °F
ISO 527-2
Elongation at Break 1.7 %

@Temperature 23.0 °C
1.7 %

@Temperature 73.4 °F
ISO 527-2
Tensile Modulus 14.0 GPa

@Temperature 23.0 °C
2030 ksi

@Temperature 73.4 °F
ISO 527-2
Flexural Strength 250 MPa

@Temperature 23.0 °C
36300 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 14.0 GPa

@Temperature 23.0 °C
2030 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.50 J/cm
8.43 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
ISO 8302
Maximum Service Temperature, Air 220 °C
428 °F
ASTM D794
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
ISO 75-2/A
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Oxygen Index 51 %
51 %
ISO 4598-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Dielectric Constant 3.9

@Frequency 1.00e+6 Hz
3.9

@Frequency 1.00e+6 Hz
IEC 60250
4.0

@Frequency 1000 Hz
4.0

@Frequency 1000 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm
432 kV/in
IEC 60243-1
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
IEC 60250
0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 150 V
150 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 290 - 300 °C
554 - 572 °F
Middle Barrel Temperature 310 - 320 °C
590 - 608 °F
Front Barrel Temperature 320 - 330 °C
608 - 626 °F
Nozzle Temperature 320 - 350 °C
608 - 662 °F
Melt Temperature 320 - 330 °C
608 - 626 °F
Mold Temperature 150 - 160 °C
302 - 320 °F
Injection Pressure 50.0 - 150 MPa
7250 - 21800 psi
Hold Pressure 30.0 - 150 MPa
4350 - 21800 psi
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi
Screw Speed 3.0 - 10 rpm
3.0 - 10 rpm
Descriptive Properties Value Comments
Additional Properties Spiral Flow Length - Internal Method: 190 mm
Forms Pellets
Injection Rate Fast
Processing Method Injection Molding
RoHS Compliance RoHS Compliant