- Zhejiang Juner PA-A6-66H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide
Zhejiang Juner PA-A6-66H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Zhejiang Juner New Materials Co. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zhejiang Juner PA-A6-66H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Cover of Mini MCBInformation provided by Zhejiang Juner New Materials Co, Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | GB/1033 |
| Water Absorption | 0.60 % | 0.60 % | 23°C•24h |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 120 MPa | 17400 psi | GB/1040 |
| Elongation at Break | 2.0 % | 2.0 % | GB/1040 |
| Flexural Strength | 200 MPa | 29000 psi | GB/9341 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | GB/9341 |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | IS0179-1:2000 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | IS0179-1:2000 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | GB1634 |
| Flammability, UL94 | V-0 | V-0 | GB/T2408 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | GB/1410 |
| Comparative Tracking Index | 550 V | 550 V | GB/4207 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 - 280 °C | 482 - 536 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 110 °C @Time 18000 sec |
230 °F @Time 5.00 hour |
Chute Hot-Wind |
| 110 °C @Time 18000 sec |
230 °F @Time 5.00 hour |
Horizontal Oven | |
| 110 °C @Time 7200 sec |
230 °F @Time 2.00 hour |
Vacuum Pressure, -0.08 MPa | |
| Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Speed of Shoot, % | 40-90 |
Users viewing this material also viewed the following:
- MV Labs BA700 Ba(NO3)2 Barium nitrate
- Hong Kun Group UV Absorber
- Ineos J60-800-178 HDPE
- Techmer ES HiFill® PA6/6 GF10 IM L BK 10% Glass Filled
- Zeon Chemicals HyTemp® 4054 AR Polyacrylate Elastomer
- Colorite Polymers 6088 Non-Phthalate 88 Series Vinyl Compound
- Azoty Tarnow™ Tarnamid® T-27 MK30 Polyamide 6 - Mineral Reinforced
- 3M Dyneon™ FG 5661 Fluoroelastomer
- Samsung Cheil Industries Infino® NH-1021 PC/ABS, Unreinforced FR
Copyright © lookpolymers.com All Rights Reserved