Cossa Polimeri ESTASAN SAN 3000 Styrene Acrylonitrile
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTASAN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTASAN SAN 3000 Styrene Acrylonitrile.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High melt flow rate, good chemical resistance, excellent dimensional stabilityInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D 955 |
| Melt Flow | 40 g/10 min @Load 10.0 kg, Temperature 220 °C |
40 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ASTM D 638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D 638 |
| Flexural Modulus | 3.70 GPa | 537 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.150 J/cm @Temperature 23.0 °C |
0.281 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 102 °C @Load 5.00 kg |
216 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 108 °C @Load 0.999 kg |
226 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- Victrex® PEEK 600P Polyetheretherketone (discontinued **)
- Huntsman AroCy B-10 Monomeric Bisphenol-A Dicyanate
- KKPC KOSYN SOL 5990 Solution Styrene Butadiene Rubber (S-SBR)
- Silon TA 2343 HD Black Catalyst Masterbatch
- Teknor Apex APEX® 3200-90 Polyvinyl Chloride, Flexible
- A. Schulman POLYBATCH™ 60186U Almond Concentrate Based in LLDPE
- China Tungsten ST2175 PM Antifriction Parts
- Arlon 47091R012 0.012" (0.305 mm) Uncured Rubber with Fiberglass Substrate
- Overview of materials for Ethylene-Methyl Acrylate Copolymer, Film Grade
- NOVA Chemicals Sclair® 11B4 Octene LLDPE Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved