Wellman Wellamid® GFT15N050-N2 15% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized &n

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/Nylon 6 Blend, Glass Fiber Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Wellman Wellamid® GFT15N050-N2 15% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized &n.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equipment.Data provided by the manufacturer, Wellman Inc.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	ISO 1183
Water Absorption	1.2 %	1.2 %	Approximate 24 hr.
Linear Mold Shrinkage	0.0060 - 0.010 cm/cm	0.0060 - 0.010 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	95.0 MPa	13800 psi	ISO 527
Elongation at Break	4.0 %	4.0 %	ISO 527
Flexural Yield Strength	150 MPa	21800 psi	ISO 178
Flexural Modulus	4.30 GPa	624 ksi	ISO 178
Izod Impact, Notched	1.50 J/cm	2.81 ft-lb/in	ISO 180

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO 75
Flammability, UL94	HB @Thickness 0.790 mm	HB @Thickness 0.0311 in	From Wellman QC Laboratory Testing; UL 94

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	282 - 310 °C	540 - 590 °F
Middle Barrel Temperature	277 - 304 °C	530 - 580 °F
Front Barrel Temperature	271 - 299 °C	520 - 570 °F
Nozzle Temperature	271 - 304 °C	520 - 580 °F
Melt Temperature	271 - 304 °C	520 - 580 °F
Mold Temperature	71.1 - 93.3 °C	160 - 200 °F
Drying Temperature	79.4 °C	175 °F	Opened bags and gaylord boxes
Dry Time	2 - 4 hour	2 - 4 hour	Opened bags and gaylord boxes
Moisture Content	0.050 - 0.20 %	0.050 - 0.20 %	During molding to prevent hydrolytic degradation
	<= 0.20 %	<= 0.20 %	In shipping bags, ready to mold
Injection Pressure	34.5 - 138 MPa	5000 - 20000 psi
Back Pressure	0.345 MPa	50.0 psi
Screw Speed	30 - 120 rpm	30 - 120 rpm