Chengdu Polyster 7502 High Performance Grade TPV
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV) |
| Manufacturer | Chengdu Polyster Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chengdu Polyster 7502 High Performance Grade TPV.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent resiliency, good hand feel, paintable.Information provided by Chengdu Polyster Co., Ltd.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | GB 2411 |
| Tensile Strength, Ultimate | 8.10 MPa | 1170 psi | GB/T 528 |
| Elongation at Break | 450 % | 450 % | GB/T 528 |
| Tear Strength | 51.0 kN/m | 291 pli | GB/T 529 |
| Compression Set | 25 % @Temperature 23.0 °C |
25 % @Temperature 73.4 °F |
GB/T 7759 |
| 40 % @Temperature 100 °C |
40 % @Temperature 212 °F |
GB/T 7759 | |
| Tensile Set | 18 % | 18 % | 100%; GB/T 528 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | GB 5470 |
Users viewing this material also viewed the following:
- Renegade Materials Corporation RM-5001 Cyanate Ester Prepreg, 6781 S2 Glass Fabric
- Solvay Specialty Polymers Radel® R-5900 Polyphenylsulfone (PPSU)
- Von Roll Isola IMI Varnish 73523 Solventless Polyester Varnish for Electrical Insulation
- Loctite® 5910 Form-in-place RTV Silicone Flange Sealant
- ExxonMobil HD 8660.29 Rotational Molding Resin
- Dymax 9-20275 Coil Terminating, Tamper proofing and Structural Electronic Bonder
- 3M FP011 Clear Polypropylene Label Products
- PolyOne Geon™ Vinyl Wire & Cable W1100L-xx92FRD Polyvinyl Chloride, Flexible (PVC, Flexible)
- Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved