Wellman Wellamid® FR22F-NBK3 Flame Retardant Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® FR22F-NBK3 Flame Retardant Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Flame Retardant Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183-87 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527-93 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527-93 |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178-93 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-93 |
| Flammability, UL94 | V-0 @Thickness 0.790 mm |
V-0 @Thickness 0.0311 in |
Users viewing this material also viewed the following:
- Honeywell ACLAR® 11A (3.00 mil) CTFE Homopolymer, Barrier Film (discontinued **)
- H.C. Starck HPM 1705 Tungsten High Density Composite
- LATI Latamid 66 VH G/30 PA 66, 30% Glass Fiber Reinforced, Heat Stabilized
- Samsung Cheil Industries Infino® SI-3109GL PC, Glass Filled High Impact
- Master Bond EP30HV Optically Clear, High Strength Two Part Epoxy
- Polyram RamLloy PZF301G4 PC/PBT Alloy, 20% Glass Fiber
- A. Schulman POLYFORT™ FPP 1310 Coupled Mica Filled Homopolymer Polypropylene
- Ascend Performance Materials Vydyne® R540H Nylon 66, 40% Glass Reinforced, DAM
- DuPont Performance Polymers Neoprene 750 Polychloroprene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved