Teknor Apex Telcar® TL-1522H Thermoplastic Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Teknor Apex Company
Trade Name TELCAR®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teknor Apex Telcar® TL-1522H Thermoplastic Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets Processing Method: Extrusion; Injection Molding Injection Notes: Injection Rate: Moderate-Fast Extrusion Notes: Screw Speed: 30 to 100 rpmInformation Provided by Teknor Apex
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
ASTM D955
Melt Flow 17.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
17.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
57.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
57.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 70
70
ASTM D2240
Tensile Strength at Break 5.24 MPa
760 psi
ASTM D412
Tensile Stress 1.86 MPa

@Strain 100 %
270 psi

@Strain 100 %
ASTM D412
2.83 MPa

@Strain 300 %
410 psi

@Strain 300 %
ASTM D412
Elongation at Break 650 %
650 %
ASTM D412
Tear Strength 24.5 kN/m
140 pli
Die C; ASTM D624
Compression Set 30 %

@Temperature 22.8 °C,
Time 79200 sec
30 %

@Temperature 73.0 °F,
Time 22.0 hour
ASTM D395B
82 %

@Temperature 70.0 °C,
Time 79200 sec
82 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395B
98 %

@Temperature 100 °C,
Time 79200 sec
98 %

@Temperature 212 °F,
Time 22.0 hour
ASTM D395B
Electrical Properties Metric English Comments
Volume Resistivity 1.60e+16 ohm-cm

@Temperature 50.0 °C
1.60e+16 ohm-cm

@Temperature 122 °F
ASTM D257
7.40e+18 ohm-cm

@Temperature 22.8 °C
7.40e+18 ohm-cm

@Temperature 73.0 °F
ASTM D257
Dielectric Strength 39.4 kV/mm
1000 kV/in
ASTM D419
Processing Properties Metric English Comments
Rear Barrel Temperature 171 - 193 °C
340 - 380 °F
Middle Barrel Temperature 177 - 199 °C
350 - 390 °F
Front Barrel Temperature 182 - 204 °C
360 - 400 °F
Nozzle Temperature 188 - 210 °C
370 - 410 °F
Zone 1 166 - 188 °C
330 - 370 °F
Zone 2 171 - 193 °C
340 - 380 °F
Zone 3 177 - 199 °C
350 - 390 °F
Zone 5 182 - 204 °C
360 - 400 °F
Die Temperature 190 - 210 °C
374 - 410 °F
Melt Temperature 188 - 210 °C
370 - 410 °F
Processing Temperature
Mold Temperature 25.0 - 65.6 °C
77.0 - 150 °F
Injection Pressure 1.38 - 6.89 MPa
200 - 1000 psi
Back Pressure 0.172 - 0.345 MPa
25.0 - 50.0 psi
Cushion 0.381 - 2.54 cm
0.150 - 1.00 in
Screw Speed 50 - 100 rpm
50 - 100 rpm
Descriptive Properties Value Comments
Appearance Opaque
Copyright © lookpolymers.com All Rights Reserved