Unitika A3130 PA6, 35% Mineral Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A3130 PA6, 35% Mineral Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 % @Time 86400 sec |
1.2 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 3.20 mm |
0.0080 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ISO 2039 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527-1/-2 |
| Tensile Modulus | 6.40 GPa | 928 ksi | ISO 527-1/-2 |
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| Flexural Modulus | 6.30 GPa | 914 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.10 J/cm² | 19.5 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 196 °C | 385 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 42.1 kV/mm @Thickness 1.00 mm |
1070 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 255 - 265 °C | 491 - 509 °F | |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |
| Front Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Back Pressure | 3.00 - 5.00 MPa | 435 - 725 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Primary Pressure | 70-90 MPa | |
| Secondary Pressure | 50-70 MPa |
Users viewing this material also viewed the following:
- Polymer Resources ABS-G5-[color]-3 ABS, 5% Glass Reinforced, UV-stabilized
- Solvay Specialty Polymers Amodel® AF-1133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry As Molded
- Techmer ES HiFill® PBT GF20 20% Glass Filled
- Dow Corning SYL-OFF® 7395 COATING
- ExxonMobil Exceed™ 4518PA Premium Cast Film Resin
- Asahi Kasei Thermylene® P-40TC-8100 Chemically Coupled Polypropylene Compound, 40% Talc Filled
- BASF Ultramid® 8262G HS BK-102 7/13% Glass/Mineral Filled PA6 (Dry)
- Ashley Polymers Ashlene® 527LD-33G Nylon 66, High Impact, 33% Glass Reinforced
- Azoty Tarnow™ Alphalon™ 33 Nylon 6
Copyright © lookpolymers.com All Rights Reserved