SABIC Innovative Plastics LNP STAT-KON DDF029 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DDF029 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon, Glass Fiber. Added features of this material include: Electrically Conductive. Flame Retardant.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ASTM D792
Moisture Absorption 0.110 %
0.110 %
50% RH, 24 hrs; ASTM D570
0.200 %
0.200 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Time 86400 sec
0.0040 in/in

@Time 24.0 hour
ASTM D955
0.0044 cm/cm

@Time 86400 sec
0.0044 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0049 cm/cm

@Time 86400 sec
0.0049 in/in

@Time 24.0 hour
ISO 294
0.0050 cm/cm

@Time 86400 sec
0.0050 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 81.0 MPa
11700 psi
ASTM D638
81.0 MPa
11700 psi
ISO 527
Elongation at Break 2.8 %
2.8 %
ISO 527
2.9 %
2.9 %
ASTM D638
Tensile Modulus 4.48 GPa
650 ksi
50 mm/min; ASTM D638
4.60 GPa
667 ksi
1 mm/min; ISO 527
Flexural Strength 132 MPa
19100 psi
ASTM D790
134 MPa
19400 psi
ISO 178
Flexural Modulus 4.41 GPa
640 ksi
ASTM D790
4.80 GPa
696 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.43 J/cm
8.30 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 32.0 kJ/m²
15.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 7.00 J
5.16 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 43.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
24.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
44.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
24.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 50.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
51.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
135 °C

@Thickness 3.20 mm
275 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.80 mm
V-0

@Thickness 0.0709 in
UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Surface Resistance 1e+05 - 1.00e+10 ohm
1e+05 - 1.00e+10 ohm
ASTM D257