UBE UBESTA® 3030U Nylon 12 (After Methanol for 500 hours)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | UBE |
| Trade Name | UBESTA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBESTA® 3030U Nylon 12 (After Methanol for 500 hours).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, cleaning agents, water, seawater and other chemicals. Compared with other types of plastics, UBESTA is particularly resistant to oils, and it displays strong resistance to organic acids and metal chlorides which adversely affect Nylon 12 and Nylon 66Information provided by UBE.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 34.1 MPa | 4950 psi | 68% Ret. |
| Tensile Strength, Yield | 34.3 MPa | 4970 psi | 82% Ret. |
| Elongation at Break | 117 % | 117 % | 146% Ret. |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 °C | 446 °F | Flange Temperature for T-Die Cast Film Extrusion |
| Zone 1 | 190 °C | 374 °F | For T-Die Cast Film Extrusion |
| 230 °C | 446 °F | For 8x1 mm Tube Extrusion | |
| Zone 2 | 210 °C | 410 °F | For T-Die Cast Film Extrusion |
| 225 °C | 437 °F | For 8x1 mm Tube Extrusion | |
| Zone 3 | 220 °C | 428 °F | For 8x1 mm Tube Extrusion |
| 230 °C | 446 °F | For T-Die Cast Film Extrusion | |
| Zone 4 | 215 °C | 419 °F | For 8x1 mm Tube Extrusion |
| Die Temperature | 230 °C | 446 °F | For T-Die Cast Film Extrusion |
| Die Opening | 0.0400 cm | 0.0157 in | For T-Die Cast Film Extrusion |
| Roll Temperature | 50.0 °C | 122 °F | Chill Roll Temperature for T-Die Cast Film Extrusion |
| Drying Temperature | 80.0 °C | 176 °F | Option 1 |
| 100 °C | 212 °F | Option 2 | |
| 110 °C | 230 °F | Option 3 | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Option 3 |
| 4 - 6 hour | 4 - 6 hour | Option 2 | |
| 6 - 8 hour | 6 - 8 hour | Option 1 | |
| Screw Speed | 15 - 76 rpm | 15 - 76 rpm | For 8x1 mm Tube Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| C/R | 3-3.5:1 | For 8x1 mm Tube Extrusion |
| Calibrating Vacuum | 100 mbar | For 8x1 mm Tube Extrusion |
| Calibration | 9.95 mm | For 8x1 mm Tube Extrusion |
| Compression Ratio | min 3:1 | For 8x1 mm Tube Extrusion |
| Die Diameter | 16 mm | For 8x1 mm Tube Extrusion |
| Die Width | 300 mm | For T-Die Cast Film Extrusion |
| Extruder | Barmag, Screw Diameter = 30 mm | For T-Die Cast Film Extrusion |
| Extruder Characteristics | 65 mm screw diameter | For 8x1 mm Tube Extrusion |
| Film Thickness | 60 microns | For T-Die Cast Film Extrusion |
| Haul Off Speed | 5 m/min | For T-Die Cast Film Extrusion |
| Haul Speed | 10-55 m/min | For 8x1 mm Tube Extrusion |
| L/D Ratio | 25:1 | For 8x1 mm Tube Extrusion |
| Length of Compression Zone | 30% of screw length | For 8x1 mm Tube Extrusion |
| Length of Feeding Zone | 30-40% of screw length | For 8x1 mm Tube Extrusion |
| Length of Metering Zone | 30-45% of screw length | For 8x1 mm Tube Extrusion |
| Mandrel Diameter | 12 mm | For 8x1 mm Tube Extrusion |
| Tensile Work To Break | 727 kJ/m2 | 90% Ret. |
| Water Temperature | 10-18°C | For 8x1 mm Tube Extrusion |
Users viewing this material also viewed the following:
- Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C)
- Lubrizol ESTANE® X4928 Ether Based Thermoplastic Polyurethane (European Grade)
- Dow Corning SR-7010
- China Tungsten ZK10UF Tungsten Carbide
- Clariant Renol PA111G60 Nylon 66, 60% Glass Fiber
- Azoty Tarnow™ Tarnamid® T-27 MT30 Polyamide 6 - Mineral Reinforced
- 3M Scotchcal™ ElectroCut™ 7725-24 Graphic Film
- 3M Scotch-Weld™ 3789 Hot Melt Adhesive
Copyright © lookpolymers.com All Rights Reserved