PolyOne Geon™ HTX 92052 Polyvinyl Chloride Alloy (PVC Alloy)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ HTX 92052 Polyvinyl Chloride Alloy (PVC Alloy).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 41.3 MPa | 5990 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.90 GPa | 421 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 76.5 MPa | 11100 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.880 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.65 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256A |
| Dart Drop Total Energy | 67.2 J/cm @Temperature 23.0 °C |
0.126 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 67.2 J/cm @Temperature 23.0 °C |
0.126 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 67.0 µm/m-°C | 37.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C @Thickness 3.18 mm |
190 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 91.7 °C @Thickness 3.18 mm |
197 °F @Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.1 °C @Thickness 3.18 mm |
178 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 85.0 °C @Thickness 3.18 mm |
185 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Acceptable | |
| Forms | Cube | |
| Generic Material | PVC Alloy | |
| Generic Name | Polyvinyl Chloride Alloy (PVC Alloy) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 13255 | ASTM D1784 |
| 4-22224-53-0000 | ASTM D4216 | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Outdoor Applications | |
| Profiles |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1200THL BK Nylon 6/6
- PolyOne Dynaflex™ G7950-9001-02 Thermoplastic Elastomer (TPE)
- Lehmann & Voss LUVOCOM® 1106-8124 Polyether imide, lubricant modified
- Lotus Nano Paint NAP 201 Fast Dry Nano-paint
- Cosmic Plastics K77 Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
- DSM Arnite® TV4 290 PBT-GF50
- DuPont™ Appeel® 11D888 Ethylene Vinyl Acetate
- ChevronTexaco Supreme SAE 30 Motor Oil
- Eurotec® Tecomid® NA40 NL FA50 PA6.6, unfilled, flame retardant - halogen free, natural
- Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 22% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved