UBE UBESTA® 3030JLX2 Plasticized Automotive Grade Nylon 12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | UBE |
| Trade Name | UBESTA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBESTA® 3030JLX2 Plasticized Automotive Grade Nylon 12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBE UBESTA® Automotive grade Nylon 12Comments: semi-plasticized, UV resistance, heat resistanceInformation provided by UBE.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Tensile Strength at Break | >= 56.0 MPa | >= 8120 psi | ASTM D638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D638 |
| Flexural Strength | 26.0 MPa | 3770 psi | ASTM D790 |
| Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 176 °C | 349 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 °C | 446 °F | Flange Temperature for T-Die Cast Film Extrusion |
| Feed Temperature | 40.0 °C | 104 °F | Injection Molding |
| Zone 1 | 190 °C | 374 °F | For T-Die Cast Film Extrusion |
| 210 °C | 410 °F | Injection Molding | |
| 230 °C | 446 °F | For 8x1 mm Tube Extrusion | |
| Zone 2 | 210 °C | 410 °F | For T-Die Cast Film Extrusion |
| 220 °C | 428 °F | Injection Molding | |
| 225 °C | 437 °F | For 8x1 mm Tube Extrusion | |
| Zone 3 | 220 °C | 428 °F | For 8x1 mm Tube Extrusion |
| 230 °C | 446 °F | For T-Die Cast Film Extrusion | |
| 230 °C | 446 °F | Injection Molding | |
| Zone 4 | 215 °C | 419 °F | For 8x1 mm Tube Extrusion |
| 230 °C | 446 °F | Injection Molding | |
| Zone 5 | 220 °C | 428 °F | Injection Molding |
| Die Temperature | 230 °C | 446 °F | For T-Die Cast Film Extrusion |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Injection Velocity | 100 mm/sec | 3.94 in/sec | Injection Molding |
| Die Opening | 0.0400 cm | 0.0157 in | For T-Die Cast Film Extrusion |
| Roll Temperature | 50.0 °C | 122 °F | Chill Roll Temperature for T-Die Cast Film Extrusion |
| Drying Temperature | 80.0 °C | 176 °F | Option 1 |
| 100 °C | 212 °F | Option 2 | |
| 110 °C | 230 °F | Option 3 | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Option 3 |
| 4 - 6 hour | 4 - 6 hour | Option 2 | |
| 6 - 8 hour | 6 - 8 hour | Option 1 | |
| Injection Pressure | 40.0 - 50.0 MPa | 5800 - 7250 psi | Injection Molding (Injection pressure should be increased when molding thin wall parts. Pressure up to 75 bar can be used here.) |
| Hold Pressure | 25.0 - 50.0 MPa | 3630 - 7250 psi | Injection Molding |
| Back Pressure | 5.00 MPa | 725 psi | Injection Molding |
| Screw Speed | 15 - 76 rpm | 15 - 76 rpm | For 8x1 mm Tube Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| C/R | 3-3.5:1 | For 8x1 mm Tube Extrusion |
| Calibrating Vacuum | 100 mbar | For 8x1 mm Tube Extrusion |
| Calibration | 9.95 mm | For 8x1 mm Tube Extrusion |
| Compression Ratio | 2.5-3.5:1 | Injection Molding |
| min 3:1 | For 8x1 mm Tube Extrusion | |
| Die Diameter | 16 mm | For 8x1 mm Tube Extrusion |
| Die Width | 300 mm | For T-Die Cast Film Extrusion |
| Extractables | 7% | Tolerance (DIN 73378 EtOH 18hr) 2% |
| Extruder | Barmag, Screw Diameter = 30 mm | For T-Die Cast Film Extrusion |
| Extruder Characteristics | 65 mm screw diameter | For 8x1 mm Tube Extrusion |
| Film Thickness | 60 microns | For T-Die Cast Film Extrusion |
| Flight Depth in the Feeding Zone | 10-15% of Screw Diameter | Injection Molding |
| Flight Depth in the Metering Zone | 5-7% of Screw Diameter | Injection Molding |
| Haul Off Speed | 5 m/min | For T-Die Cast Film Extrusion |
| Haul Speed | 10-55 m/min | For 8x1 mm Tube Extrusion |
| L/D Ratio | 25:1 | For 8x1 mm Tube Extrusion |
| min 20:1 | Injection Molding | |
| Length of Compression Zone | 25-45% of total screw length | Injection Molding |
| 30% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Feeding Zone | 20-40% of total screw length | Injection Molding |
| 30-40% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Metering Zone | 30-45% of screw length | For 8x1 mm Tube Extrusion |
| 35-45% of total screw length | Injection Molding | |
| Mandrel Diameter | 12 mm | For 8x1 mm Tube Extrusion |
| Peripheral screw speed | 10 m/min | Injection Molding |
| Water Temperature | 10-18°C | For 8x1 mm Tube Extrusion |
Users viewing this material also viewed the following:
- PEAK Werkstoff DISPAL S693 Aluminum Alloy, AlCu5Ti, Condition T6
- Qualchem Danamid FGFLX2-30 Polyamide 6, 30% Glass Fiber
- Huntsman IROGRAN® A 85 P 4380 TPU-Polyether
- Haynes Multimet® alloy, GTAW, 3.2 mm sheet
- Multibase Multibatch® MP 50004 Anti-split
- SABIC Innovative Plastics LNP LUBRILOY RF206XXH PA 66
- Tipco Tipcofil® KMX 800 FR - UL94-V0 Flame Retardant, Highly Filled PBT/PC Alloy, with High Heat Stability
- ExxonMobil Mobil Vaculine 1419
- A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Carmel Olefins CAPILENE® M 45 F Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved