Special Metals DURANICKEL® 301 (UNS N03301) Hot-Finished and Aged Rod and Bar
| Category | Metal , Nonferrous Metal , Nickel Alloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | DURANICKEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals DURANICKEL® 301 (UNS N03301) Hot-Finished and Aged Rod and Bar.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Hot-Finished and Aged Rod and Bar specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the alloy in general.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.19 g/cc | 0.296 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 300 - 375 | 300 - 375 | 3000 kg |
| Hardness, Rockwell C | 32 - 42 | 32 - 42 | |
| Tensile Strength, Ultimate | 1100 - 1380 MPa | 160000 - 200000 psi | |
| Tensile Strength, Yield | 793 - 1030 MPa @Strain 0.200 % |
115000 - 150000 psi @Strain 0.200 % |
|
| Elongation at Break | 15 - 30 % | 15 - 30 % | |
| Modulus of Elasticity | 207 GPa | 30000 ksi | Tension |
| Poissons Ratio | 0.31 | 0.31 | |
| Fatigue Strength | 350 MPa @# of Cycles 1.00e+8 |
50800 psi @# of Cycles 1.00e+8 |
rotating beam (Aging - 595°C/16 h F.C. to 540°C, AC) |
| Shear Modulus | 76.0 GPa | 11000 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| 14.0 µm/m-°C @Temperature 21.0 - 300 °C |
7.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean | |
| 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean | |
| 16.6 µm/m-°C @Temperature 21.0 - 900 °C |
9.22 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean | |
| Thermal Conductivity | 23.8 W/m-K | 165 BTU-in/hr-ft²-°F | |
| Melting Point | 1400 - 1440 °C | 2550 - 2620 °F | |
| Solidus | 1400 °C | 2550 °F | |
| Liquidus | 1440 °C | 2620 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 4.0 - 4.75 % | 4.0 - 4.75 % | |
| Carbon, C | <= 0.30 % | <= 0.30 % | |
| Copper, Cu | <= 0.25 % | <= 0.25 % | |
| Iron, Fe | <= 0.60 % | <= 0.60 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Nickel, Ni | >= 93 % | >= 93 % | Including Cobalt |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Titanium, Ti | 0.25 - 1.0 % | 0.25 - 1.0 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000424 ohm-cm | 0.0000424 ohm-cm | |
| Curie Temperature | <= 95.0 °C | <= 203 °F |
Users viewing this material also viewed the following:
- Resin Technology Group Fusion 902 Odorless, Non-Frosting Fusion Cyanoacrylate
- SABIC Innovative Plastics LNP STAT-KON DEL33EC PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP PF00A PA 6 (Asia Pacific)
- Toho Tenax Besfight® G40-800 24K IMA5C EP03 Continuous Filament Carbon Fiber
- Total PPC 7652 Polypropylene, Heterophasic Copolymer, Injection Molding
- ChevronTexaco Cygnus® 100 Hydraulic Oil
- 3M HDT Heat Shrink Tubing
- Addcomp ADD-VANCE® SA 420 Slip/anti-block additive
- DuPont Performance Polymers Minlon® 11C140 NC010 Nylon 66 (Unverified Data**)
- Cheng Yu Plastic ML3410 PC, 10% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved