Toyobo GLAMIDE® NB-1700 Nylon/Olefin
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® NB-1700 Nylon/Olefin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade NB-1700 is a non-reinforced alloy of nylon and olefin. It is light weight and has low water absorption.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | Absolute Drying; ASTM-D792 |
| Water Absorption | 1.1 % | 1.1 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0070 - 0.010 cm/cm @Thickness 1.00 mm |
0.0070 - 0.010 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.014 - 0.018 cm/cm @Thickness 3.00 mm |
0.014 - 0.018 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 25 - 30 g/10 min | 25 - 30 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 11.0 MPa @Temperature 80.0 °C |
1600 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.4%); ASTM-D638 |
| 14.0 MPa @Temperature 80.0 °C |
2030 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 34.0 MPa @Temperature 23.0 °C |
4930 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.4%); ASTM-D638 | |
| 55.0 MPa @Temperature 23.0 °C |
7980 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 90.0 MPa @Temperature -40.0 °C |
13100 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.4%); ASTM-D638 | |
| 95.0 MPa @Temperature -40.0 °C |
13800 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | >= 100 % | >= 100 % | Absolute Drying; ASTM-D638 |
| >= 200 % | >= 200 % | Practical Use (Water Absorption 2.4%); ASTM-D638 | |
| Flexural Strength | 15.0 MPa @Temperature 80.0 °C |
2180 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 |
| 19.0 MPa @Temperature 80.0 °C |
2760 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 48.0 MPa @Temperature 23.0 °C |
6960 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 | |
| 77.0 MPa @Temperature 23.0 °C |
11200 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 125 MPa @Temperature -40.0 °C |
18100 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 | |
| 130 MPa @Temperature -40.0 °C |
18900 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 0.300 GPa @Temperature 80.0 °C |
43.5 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 |
| 0.700 GPa @Temperature 80.0 °C |
102 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 0.900 GPa @Temperature 23.0 °C |
131 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 | |
| 2.20 GPa @Temperature 23.0 °C |
319 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 3.10 GPa @Temperature -40.0 °C |
450 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.4%); ASTM-D790 | |
| 3.50 GPa @Temperature -40.0 °C |
508 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C |
0.749 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.600 J/cm @Temperature -40.0 °C |
1.12 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.4%); ASTM-D256 | |
| 1.05 J/cm @Temperature 23.0 °C |
1.97 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 4.50 J/cm @Temperature 23.0 °C |
8.43 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 2.4%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Practical Use (Water Absorption 2.4%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 14.0 kV/mm @Thickness 2.00 mm |
356 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.4%); ASTM-D149 |
| 18.0 kV/mm @Thickness 2.00 mm |
457 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 110 sec | 110 sec | Practical Use (Water Absorption 2.4%); ASTM-D495 |
| 125 sec | 125 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 245 - 285 °C | 473 - 545 °F | |
| Mold Temperature | 30.0 - 80.0 °C | 86.0 - 176 °F | |
| Injection Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi |
Users viewing this material also viewed the following:
- MV Labs DY300 Dy2(CO3)3·xH2O Dysprosium carbonate hydrate
- Lehmann & Voss ELECTRAFIL M-2386 Polycarbonate, with carbon fiber and PTFE
- Multibase Multi-Flex® A 7727 E Black TPE Thermoplastic Elastomer
- Schwartz Technical Plastics LAMIGAMID® 309 Cast Polyamide 6, Oil Filled, Conditioned
- Tra-Con Tra-Bond FS469 Clear High Strength Epoxy
- ELASTO UK Dryflex® 660750S SEBS Based Material, Semi-Filled Qualities, 75A Hardness, Natural
- BASF Dimethylformamide
Copyright © lookpolymers.com All Rights Reserved