BASF Ultramid® 1403-2 BK ND3007 PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1403-2 BK ND3007 PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption | 7.4 % | 7.4 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |
| Tensile Modulus | 6.00 GPa | 870 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | ASTM Test |
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM Test |
| 5.80 GPa | 841 ksi | ISO Data | |
| Izod Impact, Notched (ISO) | 5.20 kJ/m² | 2.47 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179 |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179 |
| 0.450 J/cm² @Temperature -30.0 °C |
2.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ASTM Test |
| 262 °C | 504 °F | ISO 75 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 231 °C | 448 °F | ASTM Test |
| 245 °C | 473 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne Bergadur™ PB400 G15 H UF UV Polybutylene Terephthalate (PBT)
- Karina E 835-10/91-C-ERYB White PVC Compound
- UBE UBESTA® 3030U Nylon 12 (After Calcium Chloride aq. for 500 hours)
- ExxonMobil Label-Lyte® 90 LP Coated, High Sheen, Metallized, White Opaque OPP for Water-based Patch Label Applications
- Asahi Kasei Thermylene® P6-40FG-0100 40% Glass Fiber Reinforced, Heat Stabilized
- Advanced Polymer Alloys Alcryn® 4670 BK Melt Processable Rubber
- Overview of materials for Ionomer, Molded
- Polimeri Europa SINKRAL PD G120 ABS (discontinued **)
Copyright © lookpolymers.com All Rights Reserved