SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer. The resin is injection moldable and only available in black.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D 792 |
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.00 % | 0.00 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.020 % @Temperature 23.0 °C |
0.020 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 300 °C |
16 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D 638 |
| 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D 638 |
| 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 0.60 % | 0.60 % | Type I, 5 mm/min; ASTM D 638 |
| 0.60 % | 0.60 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 0.60 % | 0.60 % | 5 mm/min; ISO 527 |
| 0.60 % | 0.60 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 14.99 GPa | 2174 ksi | 1 mm/min; ISO 527 |
| 16.3 GPa | 2360 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 12.74 GPa | 1848 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 13.64 GPa | 1978 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.340 J/cm @Temperature 23.0 °C |
0.637 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 0.370 J/cm @Temperature -30.0 °C |
0.693 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 49.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 231 °C | 448 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 234 °C @Thickness 3.20 mm |
453 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 231 °C | 448 °F | Rate B/50; ASTM D 1525 |
| 233 °C | 451 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 2.00 mm |
HB @Thickness 0.0787 in |
UL 94 |
| HB @Thickness 2.00 mm |
HB @Thickness 0.0787 in |
UL 94 by SABIC-IP | |
| V-2 @Thickness 0.500 mm |
V-2 @Thickness 0.0197 in |
UL 94 by SABIC-IP | |
| V-2 @Thickness 0.500 mm |
V-2 @Thickness 0.0197 in |
UL 94 | |
| V-1 @Thickness 0.500 mm |
V-1 @Thickness 0.0197 in |
UL 94 | |
| V-1 @Thickness 0.500 mm |
V-1 @Thickness 0.0197 in |
UL 94 by SABIC-IP | |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
UL 94 by SABIC-IP | |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
UL 94 | |
| 5VB @Thickness 0.500 mm |
5VB @Thickness 0.0197 in |
UL 94 by SABIC-IP | |
| 5VA @Thickness 0.500 mm |
5VA @Thickness 0.0197 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 25000 ohm-cm | 25000 ohm-cm | ASTM D 257 |
| 25000 ohm-cm | 25000 ohm-cm | IEC 60093 | |
| Comparative Tracking Index | 100 V | 100 V | IEC 60112 |
Users viewing this material also viewed the following:
- Eastman Eastalloy DA111 PC+PET Copolyester/Polycarbonate (discontinued **)
- DuPont™ Clysar® EZ Polyolefin Shrink Packaging Film, 75 Gauge (discontinued **)
- Hogen HM1150 Tungsten-Based Metal
- FloMet 7% Ni/Fe Low Alloy Steel
- Lord Adhesives 305 General Purpose, Medium Viscosity Epoxy Adhesive
- SABIC Innovative Plastics LNP Stat-kon OX92182 PPS (Europe-Africa-Middle East)
- Teijin Panlite® LV-2225L Standard (mold release/ice color grade) Polycarbonate Resin
- Chosun Refractories HM-A Special Mortar for Sliding Gate Valve
- DuPont Teijin Films Mylar® M34 Polyester Film, 50 Gauge (13 µm), PVDC Coated
- Bapolene® 142F Polyethylene Film Grade
Copyright © lookpolymers.com All Rights Reserved