- LG Chemical LUPOY GP2300 PC+GF30%, Heat Resistance
LG Chemical LUPOY GP2300 PC+GF30%, Heat Resistance
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP2300 PC+GF30%, Heat Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC+GF30%, General Purpose, Heat ResistanceApplication: IT/OA, E&E Housing and Components, Automotive (Interior)CAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 14 g/10 min @Load 1.20 kg, Temperature 300 °C |
14 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 4.0 % @Thickness 3.20 mm |
4.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 7.35 GPa @Thickness 3.20 mm |
1070 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 1.08 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 2.02 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 300 °C | 518 - 572 °F | Injection Molding |
| Middle Barrel Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Front Barrel Temperature | 290 - 330 °C | 554 - 626 °F | Injection Molding |
| Nozzle Temperature | 290 - 330 °C | 554 - 626 °F | Injection Molding |
| Melt Temperature | 300 - 340 °C | 572 - 644 °F | Injection Molding |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | Injection Molding |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nilit RECONYL A SG30 Recycled nylon 6.6 for injection molding, 30% mineral filled
- SABIC Innovative Plastics LNP LUBRICOMP BX02715 SAN
- Isoflon PEHD 500 High Density Polyethylene
- Solvay IGEPAL® CA 897 Surfactant
- Master Bond Mastersil 711 Fast Curing One Component Silicone
- EMS-Griltech Griltex® D 1566A Heat Stabilized Copolyamide Hotmelt Adhesive (Apparel Interlinings)
- ExxonMobil LDPE LD 185GE Low Density Polyethylene Resin (European Grade)
- DuPont Performance Polymers Zytel® FG408L NC010 Nylon 66 (Unverified Data**)
- DuPont Teijin Films Teijin® Tetoron® S Polyester Film, 300 Gauge
- Momentive Performance Materials PolarTherm® PTX25 Boron Nitride (BN) Powder
Copyright © lookpolymers.com All Rights Reserved