Tipco Tipcofil® AU 027 - Unfilled Nylon-6 Compound, with High Heat Stability, for Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Tipco Industries Ltd., India |
| Trade Name | Tipcofil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tipco Tipcofil® AU 027 - Unfilled Nylon-6 Compound, with High Heat Stability, for Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 2.5 % | 2.5 % | ASTM D570 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 30 g/10 min | 30 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 73.0 MPa | 10600 psi | ASTM D638 |
| Elongation at Break | >= 20 % | >= 20 % | ASTM D638 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Vicat Softening Point | 190 °C | 374 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 235 °C | 455 °F | |
| Rear Barrel Temperature | 230 °C | 446 °F | |
| Middle Barrel Temperature | 235 °C | 455 °F | |
| Front Barrel Temperature | 240 °C | 464 °F | |
| Nozzle Temperature | 230 °C | 446 °F | |
| Mold Temperature | 70.0 °C | 158 °F | |
| Drying Temperature | 80.0 °C | 176 °F |
Users viewing this material also viewed the following:
- Overview of materials for Acetal Copolymer, 10% Glass Fiber Reinforced
- Mallard Creek Polymers ROVENE® 4170 SBR Latex
- Lubriplate AC-2 Petroleum-Based Air Compressor Fluid
- Latrobe HS-29XLâ„¢ ASTM M2-HC High Speed Steel
- SABIC Innovative Plastics LNP LUBRICOMP UCL36S PPA (Asia Pacific)
- Styron Magnumâ„¢ 3416 SC Natural Plus ABS Resin
- Solvay SOPROPHOR® 4 D 360 Surfactant
- UBE F022 Polyethylene
- Eastman Tenite Butyrate 485A2R30016 Natural Cellulose Acetate Butyrate
- Braskem LL6901S LLDPE Blown Film Extrusion Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved