Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled |
Manufacturer | |
Trade Name | |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | DSM Akulon® Ultraflow™ K-FG12 Nylon 6-60% Glass Reinforced (European Grade) (Dry)
(discontinued **).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
Water Absorption | 3.6 % | 3.6 % | Sim. to ISO 62 |
Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | Humidity Absorption; Sim. to ISO 62 |
Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 |
Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 235 MPa | 34100 psi | ISO 527-1/-2 |
Elongation at Break | 2.2 % | 2.2 % | ISO 527-1/-2 |
Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527-1/-2 |
Flexural Strength | 360 MPa | 52200 psi | ISO 178 |
Flexural Modulus | 16.5 GPa | 2390 ksi | ISO 178 |
Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C |
40.5 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
CTE, linear, Transverse to Flow | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
Descriptive Properties | Value | Comments |
---|---|---|
Injection molding | Yes | |
With Fillers | Yes |