BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. It is also available in heat stabilized (Ultramid 8331G HI HS) and/or pigmented versions.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
Melt; ISO 1183
1.34 g/cc
0.0484 lb/in³
dry; ISO 1183
Water Absorption 0.90 %
0.90 %
24 hour; ISO Test
5.5 %
5.5 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 90.0 MPa
13100 psi
5mm/min; ISO 527
Elongation at Break 6.0 %
6.0 %
5mm/min; ISO 527
6.0 %
6.0 %
0.2 in/min; ASTM Test
Tensile Modulus 4.61 GPa
669 ksi
1mm/min; ISO 527
Flexural Strength 120 MPa
17400 psi
ISO Data
124 MPa
18000 psi
ASTM Test
90.0 MPa

@Temperature 120 °C
13100 psi

@Temperature 248 °F
ASTM Test
100 MPa

@Temperature 93.0 °C
14500 psi

@Temperature 199 °F
ASTM Test
110 MPa

@Temperature 65.0 °C
16000 psi

@Temperature 149 °F
ASTM Test
297 MPa

@Temperature -40.0 °C
43100 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 4.83 GPa
701 ksi
ASTM Test
5.03 GPa
730 ksi
ISO Data
2.97 GPa

@Temperature 120 °C
431 ksi

@Temperature 248 °F
ASTM Test
3.25 GPa

@Temperature 93.0 °C
471 ksi

@Temperature 199 °F
ASTM Test
3.29 GPa

@Temperature 65.0 °C
477 ksi

@Temperature 149 °F
ASTM Test
Thermal Properties Metric English Comments
Specific Heat Capacity 1.958 J/g-°C
0.4680 BTU/lb-°F
Melt
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified Yes
Primary Processing Technique Injection Molding
Processing Injection Molding