Lubrizol Isoplast® 2510 Engineering Thermoplastic Polyurethane Resin
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Isoplast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Isoplast® 2510 Engineering Thermoplastic Polyurethane Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.17 % | 0.17 % | 24 hrs at 23°C; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D648 |
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 160 % | 160 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 1.50 GPa | 218 ksi | ASTM D638 |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
| Izod Impact, Unnotched | 1.80 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
3.37 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM D256 |
| 11.0 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
20.6 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 | |
| 12.8 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
24.0 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 68.0 J @Temperature 23.0 °C |
50.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| 68.0 J @Temperature -29.0 °C |
50.2 ft-lb @Temperature -20.2 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 81.0 µm/m-°C @Temperature 20.0 °C |
45.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | Unannealed; ASTM D648 |
| 82.0 °C | 180 °F | Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Unannealed; ASTM D648 |
| 77.0 °C | 171 °F | Annealed; ASTM D648 | |
| Vicat Softening Point | 89.0 °C | 192 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 100 % | 100 % | Gardner Gloss, 60°; ASTM D823 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 245 °C | 428 - 473 °F | |
| Mold Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |
| Drying Temperature | 85.0 - 90.0 °C | 185 - 194 °F |
Users viewing this material also viewed the following:
- Ohio Carbon Blank OCB EDM-200 Mechanical Grade Graphite
- Renegade Materials Corporation RM-3000 Bismaleimide (BMI) 6781 S2 Glass Fabric
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.0 PHR Zinc Stearate
- Wellman Wellpet® MRGF101-GY1 PET, 29% Mineral/Glass Fiber Reinforced
- BASF Elastollan R 2001 20% Glass Filled TPUR
- Schott CONTURAX® Borosilicate Glass
- CENTROPLAST CENTROSOL Acrylonitrile butadiene Styrene copolymer
- Fainplast Compounds RI 52/S Rigid PVC, Injection Molding
Copyright © lookpolymers.com All Rights Reserved