Kolon KOPA® KN333HB640BL Multi Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333HB640BL Multi Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstanding self lubrication and abrasion resistance, excellent chemical & weather resistance, high usage temperatureInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 127 MPa | 18500 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 4.6 % | 4.6 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 206 MPa | 29900 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 6.67 GPa | 967 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm | 1.10 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 255 °C | 491 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.4 @Frequency 1e+6 Hz |
3.4 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8832 E BLK
- SABIC Innovative Plastics Cycoloy® MC8200 PC+ABS (Asia Pacific)
- PolyOne Geon™ Vinyl Flexible A4DU5 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lucobit Lucofin® 1494 Chemically Modified Polyethylene
- A. Schulman PP 3489-01 Polypropylene Homopolymer
- CoorsTek YZTP Yttria Partially Stabilized Zirconia, Hipped
- DSM Novamid® 1017GH33 BK701 PA6-GF33
- Epoxy Technology EPO-TEK® 360T High Temperature Epoxy
- Polystrand ThermoPro™ IE7021X ECR X-Ply Cross-Ply Polyethylene-Glass Composite
Copyright © lookpolymers.com All Rights Reserved