Teijin Panlite® G-3120PH For Cameras, Glass Fiber Reinforced Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | Teijin |
| Trade Name | Panlite® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Panlite® G-3120PH For Cameras, Glass Fiber Reinforced Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced with 30 % of special GF and improved appearance grade.Applications:Precision machinery, electric and electronic components that need dimensional accuracy and good appearance.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 0.14 % | 0.14 % | in water, 23°C, 24h; ISO 62 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 50mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 4.00 GPa | 580 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 110 MPa | 16000 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 4.40 GPa | 638 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 20.0 °C |
33.3 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | ISO 75 |
| Vicat Softening Point | 135 °C | 275 °F | 50°C/hr, 50N; ISO 306 |
| UL RTI, Electrical | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| Flammability, UL94 | V-2 @Thickness 1.70 mm |
V-2 @Thickness 0.0669 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
IEC 60250 |
| 3.4 @Frequency 1e+6 Hz |
3.4 @Frequency 1e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243 |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering B60B Styrene Butadiene Rubber
- Global 120-PC-Natural Acrylonitrile Styrene, General Purpose Grade
- Karina E 838-10/182-ERYB White PVC Compound
- SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA 6/12 (Asia Pacific)
- Teknor Apex Telcar® TL EF-6123 Thermoplastic Elastomer
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=5, Diameter 0.4 mm)
- China Tungsten YG25C Tungsten Carbide
- Denka VINYKON M558050 PVC, M grade for soft injection molding
- 3M Scotch-Weld™ 1870 Industrial Adhesive
- ExxonMobil BB Mobil DTE Oil Double Letter Series
Copyright © lookpolymers.com All Rights Reserved