Zircar Zirconia ZYFB-6 Zirconia Boards, Discs, and Cylinders Insulation

Category Ceramic , Machinable Ceramic , Oxide , Zirconium Oxide
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zircar Zirconia ZYFB-6 Zirconia Boards, Discs, and Cylinders Insulation.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Type ZYFB Boards, Discs and Cylinders are rigid, refractory structures composed of yttria-stabilized zirconia fibers that do not undergo the usual phase transitions associated with pure zirconia. Type ZYFB is ideally suited for thermal insulation applications under conditions of ultra-high temperatures and in a variety of severe environments. ZYFB is fired at a high temperature to impart good dimensional stability up to 1650°C and can be used at higher temperatures where some additional sintering can be tolerated. It has good hot strength up to 1400°C and can be used as a self supporting setter for loads equal to twice its own weight up to this temperature.ZYFB is available in two densities. ZYFB-3 has a bulk density of 30 pcf and possesses extremely low thermal conductivity. ZYFB-6 has a bulk density of 60 pcf and is stronger than ZYFB-3. Both are zirconia bonded and have exceptional resistance to oxidizing and reducing atmospheres at high temperatures. Zirconia does, however, lose a small amount of oxygen at very high temperatures in vacuum and inert or reducing atmospheres. This reaction results in a color change from white to gray while most other properties remain essentially unchanged and insulation effectiveness is not impaired.ZYFB has exceptional resistance to most corrosive environments. It undergoes little attack by molten alkali metal chlorides and carbonates at temperatures up to 700°C and withstands aqueous solutions of alkali metal hydroxides at temperatures as high as 230°C. ZYFB will also tolerate exposure to inorganic acids at their boiling point for short lengths of time.Features: Rigid and MachinableHigh Purity Zirconia BondedTwo Densities Available 30 pcf & 60 pcfExtreme High Temperature StabilityFibers Stabilized with ~10 wt% YttriaLow Thermal ConductivityCan be Cemented with Zircar Zirconia Cement Type ZR-CEMCan be Surface Hardened with Zircar Zirconia Rigidizer Type ZR-RIGPre-fired and Organic FreeInformation provided by Zircar Zirconia.
Physical Properties Metric English Comments
Bulk Density 0.960 g/cc
0.0347 lb/in³
Porosity 84 %
84 %
Outgassing - Total Mass Loss 0.00 %
0.00 %
In vacuum
Mechanical Properties Metric English Comments
Flexural Strength 2.10 MPa
305 psi
Parallel to thickness
Compressive Yield Strength 1.59 MPa
231 psi
Parallel to thickness @ 10% compression
Thermal Properties Metric English Comments
CTE, linear 10.7 µm/m-°C

@Temperature 20.0 - 1180 °C
5.94 µin/in-°F

@Temperature 68.0 - 2160 °F
Thermal Conductivity 0.160 W/m-K

@Temperature 400 °C
1.11 BTU-in/hr-ft²-°F

@Temperature 752 °F
0.190 W/m-K

@Temperature 800 °C
1.32 BTU-in/hr-ft²-°F

@Temperature 1470 °F
0.220 W/m-K

@Temperature 1100 °C
1.53 BTU-in/hr-ft²-°F

@Temperature 2010 °F
0.250 W/m-K

@Temperature 1400 °C
1.74 BTU-in/hr-ft²-°F

@Temperature 2550 °F
0.270 W/m-K

@Temperature 1650 °C
1.87 BTU-in/hr-ft²-°F

@Temperature 3000 °F
Melting Point 2590 °C
4690 °F
Maximum Service Temperature, Air 2000 °C
3630 °F
Softening Point 1240 °C
2260 °F
Dilatometric @ 10psi
Shrinkage 1.00 %

@Temperature 1650 °C,
Time 3600 sec
1.00 %

@Temperature 3000 °F,
Time 1.00 hour
perpendicular to thickness
1.70 %

@Temperature 1650 °C,
Time 86400 sec
1.70 %

@Temperature 3000 °F,
Time 24.0 hour
perpendicular to thickness
Component Elements Properties Metric English Comments
HfO2 1.0 - 2.0 %
1.0 - 2.0 %
Y2O3 10 %
10 %
ZrO2 88 - 89 %
88 - 89 %