- Dow DOWLEX™ 2056G Linear Low Density Polyethylene
Dow DOWLEX™ 2056G Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2056G Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Improved thermal stability Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.28 MPa | 1491 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.03 MPa | 1455 psi | ASTM D882 |
| Film Elongation at Break, MD | 547 % | 547 % | ASTM D882 |
| Film Elongation at Break, TD | 654 % | 654 % | ASTM D882 |
| Secant Modulus, MD | 0.1620 GPa | 23.50 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.1955 GPa | 28.35 ksi | 2% Secant; ASTM D882 |
| Impact | 234 | 234 | [ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method |
| 1198 | 1198 | [ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882 | |
| 1302 | 1302 | [ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882 | |
| Elmendorf Tear Strength MD | 438 g | 438 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 690 g | 690 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 17.2 g/micron | 438 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 27.2 g/micron | 690 g/mil | ASTM D1922 |
| Dart Drop Test | 232 g | 0.512 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 50.34 MPa | 7301 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 36.02 MPa | 5224 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 121 °C | 250 °F | Dow Method (DSC) |
| Vicat Softening Point | 106 °C | 223 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- RheTech Products T20P252-01 20% Talc Reinforced Polypropylene Copolymer, Black
- Polimeri Europa Europrene® SOL T 190 Styrene - Isoprene Block Copolymer
- Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes
- SABIC Innovative Plastics NORYL N190 PPE+HIPS (Europe-Africa-Middle East)
- Total PSI 830 Polystyrene
- TSE Industries EcoSPRAY® SS100 Aliphatic Polyurethane Resin
- Crucible Steel CPM® REX® M35HCHS High Speed Steel, AISI M35
- EMS-Grivory Grivory® L 25 W 40 NZ PA12-I
- 3M Scotch-Weld™ MG100 LO Medical Grade Instant Adhesive
- Radici Radilon® S 38F (dry) Nylon 6
Copyright © lookpolymers.com All Rights Reserved