SABIC Innovative Plastics Xenoy® XD1647 PBT+PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® XD1647 PBT+PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
XENOY XD1647 is a semi crystalline, impact modified PBT+PC blend, containing 15% mineral filler. It is especially developed to obtain a reduced coefficient of thermal expansion combined with good chemical resistance. The material can be painted with water based and solvent based paint systems.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 13 g/10 min @Load 5.00 kg, Temperature 250 °C |
13 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.45 GPa | 500 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 9.00 kJ/m² @Temperature 0.000 °C |
4.28 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
36.1 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 125 °C | 257 °F | Rate B/50; ISO 306 |
| 128 °C | 262 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® NL-30GF/000 FR Nylon 6/12, Glass Filled (discontinued **)
- Lehmann & Voss LUVOCOM® 80-7050 Polyacetal-copolymer, with carbon fiber
- Fujipoly Industries Sarcon® GR-m Gap Filler Pad
- Lord Adhesives 7701 Ethyl Acetate Surface Conditioner
- Multibase Multi-Flex® A 4710 S Black TPE Thermoplastic Elastomer
- Teknor Apex APEX® 3601-80 Polyvinyl Chloride, Flexible
- Chase Plastics CP Pryme® N340MGL (DAM) Nylon 6 (Utility Grade), 40% Mineral/Glass Fiber Reinforced, Internally Lubricated
- Polyram RamTough PZ513 Polycarbonate, Easy Flow, Flame Retardant
- A. Schulman POLYBATCH™ Blue 40343/4 Concentrate Based In Polyethylene
- Loxim 400 00HB Nylon 6,6
Copyright © lookpolymers.com All Rights Reserved