Styron PulseÂ® 1370 ABS + Polycarbonate

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Styron
Trade Name	Pulse®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron PulseÂ® 1370 ABS + Polycarbonate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PULSEÂ® 1370 Engineering resin offers a superior total performance with a balance of heat resistance, practical toughness, high and low temperature impact strength retention and ease of processing.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/inÂ³	ASTM Data
Water Absorption	0.15 %	0.15 %
Moisture Absorption at Equilibrium	0.32 %	0.32 %	Humidity Absorption
Linear Mold Shrinkage	0.0070 cm/cm	0.0070 in/in
Melt Flow	3.0 g/10 min @Load 3.80 kg, Temperature 230 Â°C	3.0 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM Data

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	115	115
Tensile Strength, Ultimate	44.8 MPa	6500 psi	ASTM Data
Tensile Strength, Yield	51.7 MPa	7500 psi	ASTM Data
Elongation at Break	125 %	125 %	ASTM Data
Elongation at Yield	4.0 %	4.0 %	ISO Data
Tensile Modulus	2.30 GPa	334 ksi	ISO Data.
Izod Impact, Notched	6.41 J/cm	12.0 ft-lb/in	ASTM Data
	5.34 J/cm @Temperature -50.0 Â°C	10.0 ft-lb/in @Temperature -58.0 Â°F	ASTM Data
Charpy Impact Unnotched	NB	NB	ISO Data
	NB	NB	ISO Data, Low Temp
Charpy Impact, Notched	2.50 J/cmÂ²	11.9 ft-lb/inÂ²	ISO Data, Low Temp
	6.60 J/cmÂ²	31.4 ft-lb/inÂ²	ISO Data
Impact Test	62.2 J @Temperature -30.0 Â°C	45.9 ft-lb @Temperature -22.0 Â°F	Instrumented Dart Total Energy
	62.2 J @Temperature 23.0 Â°C	45.9 ft-lb @Temperature 73.4 Â°F	Instrumented Dart Total Energy

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	73.8 Âµm/m-Â°C @Temperature 20.0 Â°C	41.0 Âµin/in-Â°F @Temperature 68.0 Â°F	ASTM data
Deflection Temperature at 1.8 MPa (264 psi)	110 Â°C	230 Â°F	Unannealed; ASTM Data
	121 Â°C	250 Â°F	annealed; ASTM Data
Vicat Softening Point	140 Â°C	284 Â°F
Flammability, UL94	HB @Thickness 1.47 mm	HB @Thickness 0.0579 in