Styron MAGNUMâ„¢ 3325 SLG Acrylonitrile Butadiene Styrene (ABS) Resin

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	Styron
Trade Name	Magnum™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron MAGNUMâ„¢ 3325 SLG Acrylonitrile Butadiene Styrene (ABS) Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Overview: Super Low Gloss, Medium Heat, Medium Impact ABS resin for injection molded automotive interior trim applications Magnum 3325 SLG can achieve 60Â° Gardner gloss levels below 2.0 with low gloss gradient across the molded part.Applications: Chrysler-MSDB-191Ford-WSB-M4D690-AGM-GMP.ABS.009Information provided by Styron

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/inÂ³	ASTM D792; ISO 1183/B
Apparent Bulk Density	0.690 g/cc	0.0249 lb/inÂ³	ASTM D1895
Linear Mold Shrinkage, Flow	0.0053 cm/cm	0.0053 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0052 cm/cm	0.0052 in/in	ISO 294-4
Melt Flow	3.1 g/10 min @Load 3.80 kg, Temperature 230 Â°C	3.1 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM D1238; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	37.0 MPa	5370 psi	ISO 527-2
	40.0 MPa	5800 psi	51 mm/min; ASTM D638
Elongation at Break	19 %	19 %	ISO 527-2/50
	22 %	22 %	51 mm/min; ASTM D638
Elongation at Yield	3.8 %	3.8 %	51 mm/min; ISO 527-2/50; ASTM D635
Tensile Modulus	1.92 GPa	278 ksi	ISO 527-2
	2.08 GPa	302 ksi	51 mm/min; ASTM D638
Flexural Strength	61.0 MPa	8850 psi	3-point, 2 mm/min; ISO 178
	64.1 MPa	9300 psi	Method I (3 point load), 1.3 mm/min; ASTM D790
Flexural Modulus	2.07 GPa	300 ksi	3-point, 2 mm/min; ISO 178
	2.14 GPa	310 ksi	Method I (3 point load), 1.3 mm/min; ASTM D790
Izod Impact, Notched	1.30 J/cm @Temperature -30.0 Â°C	2.44 ft-lb/in @Temperature -22.0 Â°F	ASTM D256
	1.90 J/cm @Temperature 23.0 Â°C	3.56 ft-lb/in @Temperature 73.4 Â°F	ASTM D256
Izod Impact, Notched (ISO)	11.0 kJ/mÂ² @Temperature -30.0 Â°C	5.23 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 180/A
	18.0 kJ/mÂ² @Temperature 23.0 Â°C	8.57 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 180/A
Charpy Impact, Notched	1.10 J/cmÂ² @Temperature -30.0 Â°C	5.23 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	1.60 J/cmÂ² @Temperature 23.0 Â°C	7.61 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA
Dart Drop, Total Energy	23.0 J @Temperature -30.0 Â°C	17.0 ft-lb @Temperature -22.0 Â°F	Peak Energy; ASTM D3763
	30.0 J @Temperature 23.0 Â°C	22.1 ft-lb @Temperature 73.4 Â°F	Peak Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	83.0 Âµm/m-Â°C @Temperature -40.0 - 100 Â°C	46.1 Âµin/in-Â°F @Temperature -40.0 - 212 Â°F	ASTM E831
CTE, linear, Transverse to Flow	90.0 Âµm/m-Â°C @Temperature -40.0 - 100 Â°C	50.0 Âµin/in-Â°F @Temperature -40.0 - 212 Â°F	ASTM E831
Deflection Temperature at 0.46 MPa (66 psi)	96.7 Â°C	206 Â°F	Unannealed; ASTM D648
	97.0 Â°C	207 Â°F	Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	82.2 Â°C	180 Â°F	Unannealed; ISO 75-2/A; ASTM D648
Vicat Softening Point	101 Â°C @Load 5.10 kg	214 Â°F @Load 11.2 lb	Rate A (50Â°C/h); ISO 306/B50; ASTM D1525
Flame Spread	24.0 mm/min	0.945 in/min	FMVSS 302

Processing Properties	Metric	English
Rear Barrel Temperature	238 Â°C	460 Â°F
Middle Barrel Temperature	249 Â°C	480 Â°F
Front Barrel Temperature	254 Â°C	489 Â°F
Nozzle Temperature	249 - 254 Â°C	480 - 489 Â°F
Melt Temperature	243 - 271 Â°C	469 - 520 Â°F
Mold Temperature	38.0 - 66.0 Â°C	100 - 151 Â°F
Drying Temperature	82.0 - 85.0 Â°C	180 - 185 Â°F
Dry Time	>= 2.00 hour	>= 2.00 hour