Styron CALIBREâ„¢ 302V-15 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 302V-15 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 300V-15 Series Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. CALIBRE 300V series products are available in 2 additive packages: CALIBRE 302V: UV stabilizer. CALIBRE 303V: Mold release and UV stabilizer.Govt. and Industry Standards: CSA (Canadian Standards Association)Underwriters Laboratory Inc. (UL) Applications:Electronic components LightingStorage Media HousingsInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/B |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 71.0 MPa | 10300 psi | ISO 527-2/50 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-2/50 |
| Elongation at Break | 150 % | 150 % | ISO 527-2/50 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-2/50 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-2/50 |
| Flexural Strength | 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.0 mm/min; ISO 178 |
| Izod Impact, Notched | 8.50 J/cm @Temperature 23.0 °C |
15.9 ft-lb/in @Temperature 73.4 °F |
ISO 180/4A |
| Charpy Impact, Notched | 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | Annealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Unannealed; ISO 75-2/A |
| 137 °C | 279 °F | Annealed; ISO 75-2/A | |
| Vicat Softening Point | 145 °C | 293 °F | ISO 306/B50 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
Solution A; IEC 60112 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 60 Polyamide 6, 60% Glass Fiber
- PlastiComp Complet® LGF50 - PA66 MT Nylon 66, 50% Long Glass Fiber Reinforced, Impact Modified
- Parker Chomerics Tecknit Consil®-R 857 Pure Silver-Filled Silicone Elastomer
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N220 Filler
- Kraton® G1651 H (SEBS) Linear Triblock Copolymer
- Lanxess Pocan® B 4225 000000 PBT, 20% Glass Fiber
- Solvay Chemicals Ethyl 3-(difluoromethyl)-1-methyl-1H-pyrazole-4-carboxylate
- Silikony Polskie Polsil OM 20 Methyl Silicone Fluid
- Master Bond MB297 Cyanoacrylate Adhesive System
- Adamas Adalon® 509 PTFE, 3% MoS2
Copyright © lookpolymers.com All Rights Reserved