DSM Arnitel® XG6029 TPC-ET
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnitel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnitel® XG6029 TPC-ET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion Grade
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | Sim. To ISO 62 |
| Moisture Absorption | 0.640 % | 0.640 % | Sim. To ISO 62 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
cm<sup>3</sup>/10min Melt Volume-flow Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 88 @Time 3.00 sec |
88 @Time 0.000833 hour |
ISO 868 |
| Hardness, Shore D | 42 @Time 3.00 sec |
42 @Time 0.000833 hour |
ISO 868 |
| Tensile Strength, Ultimate | 9.70 MPa | 1410 psi | ISO 527-1/-2 |
| Tensile Stress | 2.60 MPa @Strain 10.0 % |
377 psi @Strain 10.0 % |
ISO 527-1/-2 |
| 4.50 MPa @Strain 100 % |
653 psi @Strain 100 % |
ISO 527-1/-2 | |
| Elongation at Break | 420 % | 420 % | ISO 527-1/-2 |
| Tensile Modulus | 0.0450 GPa | 6.53 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 180 µm/m-°C | 100 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 190 µm/m-°C | 106 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 180 °C | 356 °F | 10°C/min; ISO 11357-1/-3 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.30e+12 ohm-cm | 8.30e+12 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.5 | 3.5 | IEC 60250 |
| 3.7 | 3.7 | IEC 60250 | |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | IEC 60243-1 |
Users viewing this material also viewed the following:
- Poco Graphite EDM-4 EDM Graphite
- Techmer ES HiFill® PA6/6 GF/M19 HS BK 19% Glass/Mineral Fiber Filled
- Samsung Cheil Industries Starex® NH-0300 ABS, Unreinforced FR
- TIMET TIMETAL® 1100 Titanium Alloy (Ti-6Al-2.7Sn-4Zr-0.4Mo-0.45Si)
- Arkema Group Orgalloy® LE 6010 HV Nylon Alloy, 10% Glass Fiber Reinforced (Conditioned)
- Arkema Group Pebax® Rnew 55R53 SP 01 Polyether Block Amide (PEBA)
- AK Steel ZINCGRIP® ELECTRASMOOTH® Electrogalvanized Carbon Steel, Extra Deep Drawing Steel Plus (EDDS+), Standard Grade
- Breplast Bretene TS COR HF Dark High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved