Styron CALIBREâ„¢ 200-14 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 200-14 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 200-14 polycarbonate resin is a natural, FDA compliant, 14 melt flow rate general purpose polycarbonate resin with no mold release or UV stabilizer.Govt. and Industry Standards:US FDA 21 CFR 177.1580CSAUnderwriters Laboratory (UL)EU food contact 200/72/ECApplications:Food processorsBeverage containersFood utensilsOther packaging applicationsInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/A; ASTM D792 |
| Water Absorption | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
Equilibrium, 50% RH; ISO 62; ASTM D570 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4; ASTM D955 |
| Melt Flow | 14 g/10 min @Load 1.20 kg, Temperature 300 °C |
14 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 72 | 72 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 71.0 MPa | 10300 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2/50 |
| 150 % | 150 % | 50 mm/min; ASTM D638 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-2/50 |
| 2.34 GPa | 339 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 96.5 MPa | 14000 psi | Method I (3 point load), 2.0 mm/min; ASTM D790 |
| 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 | |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.0 mm/min; ISO 178 |
| 2.41 GPa | 350 ksi | Method I (3 point load), 2.0 mm/min; ASTM D790 | |
| Izod Impact, Notched | 8.50 J/cm @Temperature 23.0 °C |
15.9 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Notched (ISO) | 82.0 kJ/m² @Temperature 23.0 °C |
39.0 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256; ISO 180 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Impact Strength | 462 kJ/m² | 220 ft-lb/in² | ASTM D1822 |
| Dart Drop, Total Energy | 87.0 J | 64.2 ft-lb | 3.39 m/sec; ASTM D3763 |
| Abrasion | 45 | 45 | [%] Taber; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | Annealed; ISO 75-2/B; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Unannealed; ASTM D648 |
| 127 °C | 261 °F | Unannealed; ISO 75-2/A | |
| 140 °C | 284 °F | Annealed; ISO 75-2/B; ASTM D648 | |
| Vicat Softening Point | 148 °C @Load 5.10 kg |
298 °F @Load 11.2 lb |
Rate A (50°C/h); ISO 306/B50; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 26 % | 26 % | ISO 4589-2 |
| Glow Wire Test | 849 °C @Thickness 2.00 mm |
1560 °F @Thickness 0.0787 in |
IEC 60695-2-13 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542; ISO 489 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+18 ohm-cm | 2.00e+18 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
ASTM D150 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| 17.0 kV/mm | 432 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0010 @Frequency 50.0 Hz |
0.0010 @Frequency 50.0 Hz |
ASTM D150 |
| 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
Solution A; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Average Extent of Burring | 3 cm | ASTM D635 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF20 - PA6 Nylon 6, 20% Long Glass Fiber Reinforced
- Potters Industries Q-Cel® 300
- Ferro IX 2443 Passivation Glasses - High Voltage (Zn-B-Silicates)
- Momentive Performance Materials HCPL Boron Nitride (BN) Powder
- A. Schulman INVISION™ VX-5060UI INVISIONTMSoft Touch Polyolefin Thermoplastic
- Williams Advanced Alloys Wambraze™ WB949 Solder
- A. Schulman POLYBATCH™ AF-1085 Antifog Concentrate
- Aaron Industries AAROLENE® ARPS MI 100-2 Polystyrene Compounded Resin
- Polyplastics Duracon® M25-45 Acetal Co-polymer (POM), Weather resistance, High viscosity
- Iran Petrochemical (PCC) TPC - 326 WP Expandable Polystyrene
Copyright © lookpolymers.com All Rights Reserved